Hard-facing alloys having improved crack resistance
View Patent ↗Weld deposit compositions with improved crack resistance, improved wear resistance, and improved hardness are provided by controlling matrix grain size and balancing Titanium and/or Niobium with Carbon and/or Boron content. Additionally, the presence of coarse chromium carbides is drastically decreased to reduce the amount of check-cracking. Preferably, the weld deposit is produced from a flux-cored or metal-cored wire. The weld deposit characteristics include a matrix having a fine grain size, small evenly dispersed carbides within the matrix, and a small amount of Carbon in the matrix.
1. A weld deposit composition produced from a flux-cored welding wire consisting of, by percent mass:
between 0.7% and 2.0% Carbon;
between 0.1% and 0.5% Manganese;
between 0.7% and 1.4% Silicon;
between 6.0% and 11.0% Chromium;
between 0.5% and 2.0% Molybdenum;
between 2.0% and 8.0% sum of Niobium and Titanium;
between 0.2% and 1.0% Vanadium;
between 0.2% and 0.9% Boron;
between 0.4% and 0.8% Copper; and
a balance comprising Iron;
wherein amounts of Titanium and Niobium are balanced with amounts of Carbon and Boron to form intermetallic carbides and borides that act as grain refiners; the ratio of Titanium or Niobium to Boron being about 4.4 for Titanium Boride, about 2.2 for Titanium Diboride, about 8.6 for Niobium Boride, and about 4.3 for Niobium Diboride.
2. The weld deposit composition according to claim 1 , wherein the Carbon comprises approximately 1.1%.
3. The weld deposit composition according to claim 1 , wherein the Manganese comprises approximately 0.2%.
4. The weld deposit composition according to claim 1 , wherein the Silicon comprises approximately 1.0%.
5. The weld deposit composition according to claim 1 , wherein the Chromium comprises approximately 9.0%.
6. The weld deposit composition according to claim 1 , wherein the Molybdenum comprises approximately 0.8%.
7. The weld deposit composition according to claim 1 , wherein the Niobium and Titanium comprise approximately 3.5%.
8. The weld deposit composition according to claim 1 , wherein the Vanadium comprises approximately 0.3%.
9. The weld deposit composition according to claim 1 , wherein the Boron comprises approximately 0.5%.
10. The weld deposit composition according to claim 1 , wherein the Copper comprises approximately 0.6%.
11. A flux-cored welding wire capable of producing a weld deposit composition consisting of, by percent mass:
between 0.7% and 2.0% Carbon;
between 0.1% and 0.5% Manganese;
between 0.7% and 1.4% Silicon;
between 6.0% and 11.0% Chromium;
between 0.5% and 2.0% Molybdenum;
between 2.0% and 8.0% sum of Niobium and Titanium;
between 0.2% and 1.0% Vanadium;
between 0.2% and 0.9% Boron;
between 0.4% and 0.8% Copper; and
a balance comprising Iron;
wherein amounts of Titanium and Niobium are balanced with amounts of Carbon and Boron to form intermetallic carbides and borides that act as grain refiners; the ratio of Titanium or Niobium to Boron being about 4.4 for Titanium Boride, about 2.2 for Titanium Diboride, about 8.6 for Niobium Boride, and about 4.3 for Niobium Diboride.
12. A welded structure comprising at least one weld deposit, the weld deposit having a composition consisting of, by percent mass:
between 0.7% and 2.0% Carbon;
between 0.1% and 0.5% Manganese;
between 0.7% and 1.4% Silicon;
between 6.0% and 11.0% Chromium;
between 0.5% and 2.0% Molybdenum;
between 2.0% and 8.0% sum of Niobium and Titanium;
between 0.2% and 1.0% Vanadium;
between 0.2% and 0.9% Boron;
between 0.4% and 0.8% Copper; and
a balance comprising Iron;
wherein amounts of Titanium and Niobium are balanced with amounts of Carbon and Boron to form intermetallic carbides and borides that act as grain refiners; the ratio of Titanium or Niobium to Boron being about 4.4 for Titanium Boride, about 2.2 for Titanium Diboride, about 8.6 for Niobium Boride, and about 4.3 for Niobium Diboride.
13. The weld deposit composition according to claim 1 , wherein the carbides are evenly dispersed within a matrix of the weld deposit composition.
14. The weld deposit composition according to claim 1 , wherein the weld deposit composition has a hardness value of 63 to 65 HRC.
15. The weld deposit composition according to claim 1 , wherein the carbides have a size less than 0.1 mm.
16. The weld deposit composition according to claim 1 , wherein a matrix of the weld deposit composition has grains with a grain size less than 0.1 mm.