Three part dental bonding compositions and methods of use
View Patent ↗Three part bonding compositions that include an etching solution, a preparative solution, and a curable composition, as well as packaged products and methods of use for the treatment of bone substrate, i.e., teeth, are described. The etch solutions generally include an inorganic acid, an organic acid, an ethylenically unsaturated functional monomer and, optionally a solvent, and water. The preparative solutions generally include an ethylenically unsaturated functional monomer, at least one polyethylenically unsaturated functional crosslinking monomer, a photo initiator, and at least one solvent. The curable composites include reactive monomers and crosslinking agents that are effective to adhere to the surface of the treated substrate. The methods of the invention provide the ability to modify a bone or bone-like surface so that the curable composition, such as an adhesive resin, can be used in combination with a restorative material.
1. A three part dental bonding system, comprising:
(a) an etch solution comprising an inorganic acid, present in an amount of from about 1 to about 10 parts by weight; an organic acid, present in amount from about 0.1 to about 10 parts by weight; a solvent present in an amount from 0 to about 65 parts by weight; an ethylenically unsaturated functional monomer, present in an amount from about 0.1 to about 10 parts by weight and water, present in an amount from 0 to about 50 parts by weight, all components in an amount to equal a total of 100 parts by weight;
(b) a preparative solution comprising an ethylenically unsaturated functional monomer, present in an amount of from about 5 to about 25 parts by weight; a polyethylenically unsaturated functional crosslinking monomer, present in an amount of from about 10 to about 40 parts by weight; a solvent present in an amount from 0 to about 65 parts by weight; and water, present in an amount from 0 to about 50 parts by weight, all components in an amount to equal a total of 100 parts by weight; and
(c) a curable composite comprising an ethylenically unsaturated functional monomer, present in an amount of from about 10 to about 30 parts by weight; a polyethylenically unsaturated functional crosslinking monomer, present in an amount of from about 50 to about 90 parts by weight; a solvent present in an amount from 0 to about 15 parts by weight; and water, present in an amount from 0 to about 15 parts by weight, all components in an amount to equal a total of 100 parts by weight.
2. A three part dental bonding system, comprising:
(a) an etch solution comprising nitric acid, present in an amount of from about 1 to about 10 parts by weight; succinic acid, present in amount from about 0.1 to about 10 parts by weight; methacrylic acid, present in an amount from about 0.1 to about 10 parts by weight and water, present in an amount to equal a total of 100 parts by weight;
(b) a preparative solution comprising hydroxymethylacrylate, present in an amount of from about 5 to about 25 parts by weight; a reaction product of pyromellitic dianhydride with glycerol dimethacrylate (PMGDM), present in an amount of from about 15 to about 25 parts by weight; 2,2′-bis[4-(3-methacryloxy-2-hydroxy propoxy)-phenyl]-propane (bis-GMA), present in an amount of from about 5 to about 12 parts by weight; ethanol present in an amount from about 25 to about 35 parts by weight; and acetone, present in an amount from about 20 to about 30 parts by weight, all components in an amount to equal a total of 100 parts by weight; and
(c) a curable composite comprising hydroxymethylacrylate, present in an amount of from about 15 to about 25 parts by weight; bis-GMA, present in an amount of from about 60 to about 70 parts by weight; and PMGDM, present in an amount of from about 5 to about 15 parts by weight, all components in an amount to equal a total of 100 parts by weight.
3. A three part dental bonding system, comprising:
(a) an etch solution comprising nitric acid, present in an amount of about 5 parts by weight; succinic acid, present in amount of about 2.5 parts by weight; methacrylic acid, present in an amount of about 2.5 parts by weight and water, present in an amount to equal a total of 100 parts by weight;
(b) a preparative solution comprising hydroxymethylacrylate, present in an amount of about 15 parts by weight; a reaction product of pyromellitic dianhydride with glycerol dimethacrylate (PMGDM), present in an amount of about 20 parts by weight; 2,2′-bis[4-(3-methacryloxy-2-hydroxy propoxy)-phenyl]-propane (bis-GMA), present in an amount of about 8 parts by weight; ethanol present in an amount of about 30 parts by weight; and acetone, present in an amount of about 26 parts by weight, all components in an amount to equal a total of 100 parts by weight; and
(c) a curable composite comprising hydroxymethylacrylate, present in an amount of about 20 parts by weight; bis-GMA, present in an amount of about 66.5 parts by weight; and PMGDM, present in an amount of about 10 parts by weight; ethyl N,N-dimethyl-4-aminobenzoic acid (EDMAB), present in an amount of about 3 parts by weight; camphorquinone (CQ), present in an amount of about 0.5 parts by weight, all components in an amount to equal a total of 100 parts by weight.