Solar cell using low iron high transmission glass and corresponding method
View Patent ↗A high transmission low iron glass, that is highly oxidized, is provided for use in solar cells or the like. In certain example embodiments, the glass composition used for the glass is a low-iron type glass composition which is highly oxidized thereby permitting the glass to realize a combination of high visible transmission (Lta or T vis ), high ultraviolet (UV) and/or infrared (IR) transmission, and high total solar (TS) transmission. These features may be achieved without the need for antimony in certain example instances. The glass substrate used in a solar cell may be patterned in certain example embodiments of this invention.
1. A solar cell comprising:
a glass substrate;
first and second conductive layers with at least a photoelectric film provided therebetween;
wherein the glass substrate is of a composition comprising:
Ingredient
wt. %
SiO 2
67-75%
Na 2 O
10-20%
CaO
5-15%
total iron (expressed as Fe 2 O 3 )
0.001 to 0.05%
% FeO
<=0.0038
glass redox
<=0.12
antimony oxide
0 to less than 0.01%
cerium oxide
0 to 0.1%
wherein the glass substrate has visible transmission of at least 91%, a transmissive a* color value of −1.0 to +1.0, a transmissive b* color value of from 0 to +1.5, % TS of at least 90%, and a UV transmission of at least 80%.
2. The solar cell of claim 1 , wherein the glass substrate comprises:
% FeO
<=0.0030%
glass redox
<=0.09
IR transmission (% IR)
>=90%.
3. The solar cell of claim 1 , wherein the glass substrate has a % TS of at least 90.5%, a UV transmission of at least 84%, and comprises:
% FeO
<=0.0015%
glass redox
<=0.08.
4. The solar cell of claim 1 , wherein the glass substrate comprises MgO and has no more than 0.01% cerium oxide.
5. The solar cell of claim 1 , wherein the glass substrate contains no more than 2 ppm of at least two of erbium oxide, nickel oxide, cobalt oxide, neodymium oxide, chromium oxide, and selenium.
6. The solar cell of claim 1 , wherein the glass substrate contains no more than 2 ppm of at least four of erbium oxide, nickel oxide, cobalt oxide, neodymium oxide, chromium oxide, and selenium; and wherein the glass substrate has no more than 0.01% cerium oxide.
7. The solar cell of claim 1 , wherein the glass substrate contains no more than 2 ppm of at least five of erbium oxide, nickel oxide, cobalt oxide, neodymium oxide, chromium oxide, and selenium.
8. The solar cell of claim 1 , wherein the glass substrate contains no more than 2 ppm of each of erbium oxide, nickel oxide, cobalt oxide, neodymium oxide, chromium oxide, and selenium.
9. The solar cell of claim 1 , wherein the glass substrate comprises at least 0.25% SO 3 .
10. The solar cell of claim 1 , wherein the glass substrate comprises at least 0.29% SO 3 .
11. A solar cell comprising:
a glass substrate;
at least a first conductive layers and a photoelectric film;
wherein the glass substrate is of a composition comprising:
Ingredient
wt. %
SiO 2
67-75%
Na 2 O
10-20%
CaO
5-15%
% FeO
<=0.0038
antimony oxide
0 to less than 0.01%
glass redox
<=0.12
cerium oxide
<=0.01%
wherein the glass substrate has visible transmission of at least 91%, a % TS of at least 90%, and a UV transmission of at least 80%.
12. The solar cell of claim 11 , wherein the glass substrate comprises from 0.15 to 7% MgO, and comprises:
% FeO
<=0.0030%
glass redox
<=0.09.
13. The solar cell of claim 11 , wherein the glass substrate has a % TS of at least 90.5%, a UV transmission of at least 84%, and comprises:
% FeO
<=0.0015%
glass redox
<=0.08.
14. The solar cell of claim 11 , wherein the glass substrate contains no more than 2 ppm of each of erbium oxide, nickel oxide, cobalt oxide, neodymium oxide, chromium oxide, and selenium.
15. The solar cell of claim 11 , wherein the glass substrate comprises at least 0.29% SO 3 .
16. The solar cell of claim 11 , wherein the glass substrate contains from about 0.010-0.045% total iron (expressed as Fe 2 O 3 ), contains from 0-0.005% antimony oxide, and contains from 0-0.1% cerium oxide.
17. The solar cell of claim 11 , wherein the glass substrate has a % TS of at least 91%, a visible transmission of at least 91.5%, and a UV transmission of at least 85%.
18. A glass composition comprising:
Ingredient
wt. %
SiO 2
67-75%
Na 2 O
10-20%
CaO
5-15%
total iron (expressed as Fe 2 O 3 )
0.001 to 0.05%
% FeO
<=0.0038
glass redox
<=0.12
antimony oxide
0 to less than 0.01%
cerium oxide
<=0.01%
wherein the glass at a reference thickness of about 4 mm has a visible transmission of at least 91%, a transmissive a* color value of −1.0 to +1.0, a transmissive b* color value of from 0 to +1.5, % TS of at least 90%, and a UV transmission of at least 80%.
19. The glass composition of claim 18 , wherein the glass composition comprises 0-0.001% cerium oxide, a glass redox of no greater than 0.08, and % FeO of no more than about 0.0015%.