Aqua blue glass composition with increased infrared absorption
A glass composition has a base and a colorant. The composition of the base is 68 to 75% SiO 2 , 10 to 18 wt. % Na 2 O, 5 to 15 wt. % CaO, 0 to 10 wt. % MgO, 0 to 5 wt. % Al 2 O 3 , and 0 to 5 wt. % K 2 O, where CaO+MgO is 6 to 15 wt. % and Na 2 O+K 2 O is 10 to 20 wt. % is provided. The composition of the colorants comprises 0.4 to 0.6 wt. % Fe 2 O 3 , 0.18 to 0.28 wt. % FeO, 0.05 to 0.3 wt. % MnO 2 , and 0 to 8 ppm Cobalt. The redox ratio of the weight of FeO to the total weight of iron is in a range of about 0.40 to about 0.58. The colored glass has an aqua color with a dominant wavelength of 489.2 nm +/−1.2 nm, an excitation purity of 7% +/−1%, and an infrared transmittance in the range of 16% to 29% at 4.0 mm thickness.
1 . A colored glass having a base and a colorant, wherein composition of the colorant by weight of the colored glass comprises:
0.4 to 0.6 wt. % Fe 2 O 3 ;
0.18 to 0.28 wt. % FeO;
0.05 to 0.3 wt. % MnO 2 ; and
0 to 8 ppm Cobalt;
wherein a redox ratio of the weight of FeO to the total weight of iron is in a range of about 0.40 to about 0.58; and
wherein the colored glass has an aqua color with a dominant wavelength of 489.2 nm +/ 31 1.2 nm, an excitation purity of 7% +/−1%, and an infrared transmittance in the range of 16% to 29% at 4.0 mm thickness.
2 . The colored glass of claim 1 wherein a redox ratio of the weight of FeO to the total weight of iron is in a range of about 0.45 to about 0.55.
3 . The colored glass of claim 1 wherein the composition of the base by weight of the colored glass includes 1.15 to 2.0 wt. % anthracite coal.
4 . The colored glass of claim 1 wherein the composition of the base by weight of the colored glass includes 1.12 to 2.35 wt. % graphite.