Master disk for magnetic transfer
View Patent ↗The present invention provides a master disk with high flexibility and high close contact property with a slave disk to be transferred, which bears information to be transferred by magnetic transfer. When incident angle of X-ray is designated by θ, electroforming is performed such that X-ray diffraction pattern of the master substrate 11 has a 200 plane reflection at 2θ=51.0° to 53.0°, and a 220 plane reflection at 2θ=75.5° to 76.5°, and the reflection intensity ratio of X-ray diffraction of the 220 plane with respect to the 200 plane is I[220]/I[200]=2 to 30.
1. A master disk for magnetic transfer, including a master substrate which is comprised of metal material having a crystal structure of face-centered cubic lattice and has a concavo-convex pattern corresponding to transfer information formed thereon, and a magnetic layer film-formed on the concavo-convex pattern of the master substrate, comprising:
a X-ray diffraction pattern of the master substrate having a 200 plane reflection at 2θ=51.0° to 53.0°, and a 220 plane reflection at 2θ=75.5° to 76.5°, when incident angle of X-ray is designated by θ; and
a reflection intensity ratio of the 220 plane with respect to the 200 plane which is I[220]/I[200]=2 to 30, when the reflection intensity of the 200 plane X-ray diffraction is designated by I[200] and the reflection intensity of the 220 plane X-ray diffraction is designated by I[220].
2. The master disk for magnetic transfer according to claim 1 , wherein the metal material is nickel (Ni).
3. A master disk for magnetic transfer, including a master substrate which is comprised of metal material having a crystal structure of face-centered cubic lattice and has a concavo-convex pattern corresponding to transfer information formed thereon, and a magnetic layer film-formed on the concavo-convex pattern of the master substrate, comprising:
a X-ray diffraction pattern of the master substrate having a 200 plane reflection at 2θ=51.0° to 53.0°, and a 111 plane reflection at 2θ=43.5° to 45.5°, when incident angle of X-ray is designated by θ; and
a reflection intensity ratio of the 111 plane with respect to the 200 plane which is I[ 111]I/I[200]=1 to 8, when the reflection intensity of the 200 plane X-ray diffraction is designated by I[200] and the reflection intensity of the 111 plane X-ray diffraction is designated by I[111].
4. The master disk for magnetic transfer according to claim 3 , wherein the metal material is nickel (Ni).
5. A master disk for magnetic transfer, including a master substrate which is comprised of metal material having a crystal structure of face-centered cubic lattice and has a concavo-convex pattern corresponding to transfer information formed thereon, and a magnetic layer film-formed on the concavo-convex pattern of the master substrate, comprising:
a X-ray diffraction pattern of the master substrate having a 200 plane reflection at 2θ=51.0° to 53.0°, and a 311 plane reflection at 2θ=92.0° to 94.0°, when incident angle of X-ray is designated by θ; and
a reflection intensity ratio of the 311 plane with respect to the 200 plane which is I[311]/I[200]=0.3 to 3.0, when the reflection intensity of the 200 plane X-ray diffraction is designated by I[200] and the reflection intensity of the 311 plane X-ray diffraction is designated by I[311].
6. The master disk for magnetic transfer according to claim 5 , wherein the metal material is nickel (Ni).
7. A master disk for magnetic transfer, including a master substrate which is comprised of metal material having a crystal structure of face-centered cubic lattice and has a concavo-convex pattern corresponding to transfer information formed thereon, and a magnetic layer film-formed on the concavo-convex pattern of the master substrate, comprising:
a X-ray diffraction pattern of the master substrate having a 200 plane reflection at 2θ range of 51.0° to 53.0°, a 220 plane reflection at 2θ=75.5° to 76.5°, and a 111 plane reflection at 2θ=43.5° to 45.5°, when incident angle of X-ray is designated by θ; and
a reflection intensity ratio of a 111 plane with respect to a 200 plane which is I[111]/I[200]=1 to 8 and a reflection intensity ratio of a 220 plane with respect to a 200 plane which is I[220]/I[200]=2 to 25, when the reflection intensity of the 200 plane X-ray diffraction is designated by I[200], the reflection intensity of the 220 plane X-ray diffraction is designated by I[220], and the reflection intensity of the 111 plane X-ray diffraction is designated by I[111].
8. The master disk for magnetic transfer according to claim 7 , wherein the metal material is nickel (Ni).