View Patent ↗The present invention is directed to a method for making electrode active materials represented by the general formula: A a (VO) b XO 4 , wherein: (a) A is an alkali metal or mixture of alkali metals, and 0<a<4; (b) 0<b<2; (c) X is selected from the group consisting of phosphorous (P), sulfur (S), arsenic (As), silicon (Si), and combinations thereof; and wherein A, X, a and b are selected to maintain the electroneutrality of the electrode active material in its nascent (as prepared or synthesized) state.
1. A method for making a compound represented by the general formula:
A a (VO) b XO 4 ,
wherein:
(a) A is an alkali metal or mixture of alkali metals and 0<a≦2;
(b) X is selected from the group consisting of phosphorous (P), sulfur (S), arsenic (As), silicon (Si), and combinations thereof; and
(c) A, X, a and b are selected to maintain the electroneutrality of the compound;
the method comprising the steps of:
forming an acidic aqueous solution comprising vanadyl ions, ions of an alkali metal, and ions of XO 4 , wherein the step of forming the acidic aqueous solution comprises the step of dissolving one or more vanadyl precursor compounds, one or more alkali metal precursor compounds, and one or more precursor compounds containing moiety XO 4 , in an aqueous solvent; wherein the aqueous solution has a pH≦5 at standard temperature and pressure;
wherein:
the one or more vanadyl precursor compounds is selected from the group consisting of V 2 O 5 , V 2 O 3 , VOSO 4 , VOC 2 O 4 , and mixtures thereof;
the one or more alkali metal precursor compounds and the one or more precursor compounds containing moiety XO 4 are the same compound and is selected from the group consisting of A 2 SO 4 , A 4 SiO 4 , AH 2 PO 4 , A 3 PO 4 , HAsA 2 O 4 , and mixtures thereof,
wherein A is an alkali metal; and
precipitating the compound from the acidic aqueous solution.
2. The method of claim 1 , wherein 0≦pH≦4 at standard temperature and pressure.
3. The method of claim 2 , wherein 2≦pH≦4.
4. The method of claim 1 , wherein the step of dissolving one or more vanadyl precursor compounds, one or more alkali metal precursor compounds, and one or more precursor compounds containing moiety XO 4 , in an aqueous solvent, is a single step dissolution reaction.
5. The method of claim 1 , wherein the step of dissolving one or more vanadyl precursor compounds, one or more alkali metal precursor compounds, and one or more precursor compounds containing moiety XO 4 , in an aqueous solvent, further comprises the step of adding an acidic buffer in an amount sufficient to adjust the pH to ≦5.
6. The method of claim 1 , wherein A is selected from the group consisting of Li, Na, K, and mixtures thereof.
7. The method of claim 1 , wherein A is Li.
8. The method of claim 1 , wherein the compound is LiVOPO 4 .