Method for producing a continuous thermoplastic coating and articles constructed therefrom
View Patent ↗This invention relates to a non-contact coating method for producing a continuous coating and articles constructed therefrom. This invention further relates to a method for producing a textile material with a moisture-impermeable barrier layer and to a method for producing a moisture-absorbing article of hygiene which has such a barrier layer. This invention particularly relates to a textile material and hygienic disposable articles comprising a body fluid impermeable barrier layer produced from said coating method. Preferably, the thermoplastic composition used in the method for producing the barrier layer exhibits certain rheological characteristics.
1. A method of coating a thermoplastic composition on a substrate, said method comprising:
a) dispensing a molten thermoplastic composition from a coating device in the form of a continuous film, said thermoplastic composition comprising ethylene-vinyl acetate copolymer,
said thermoplastic composition having a complex viscosity of less than about 500 poise at about 1000 radians/second at a temperature of less than about 160° C. and a complex viscosity ranging from about 100 poise to about 1,000 poise at about 1 radian/second at a temperature of less than about 160° C.;
b) suspending the continuous film between the coating device and a substrate comprising a textile material; and
c) contacting a substrate with said continuous film to form a continuous coating of said thermoplastic composition on said substrate, said textile substrate substantially retaining its textile character.
2. The method of claim 1 , wherein the continuous film is coated on the substrate at a coat weight no greater than about 30 g/m 2 .
3. The method of claim 1 , wherein the continuous film is coated on the substrate at a coat weight no greater than about 20 g/m 2 .
4. The method of claim 1 , wherein the continuous film is coated on the substrate at a coat weight no greater than about 10 g/m 2 .
5. The method of claim 1 , wherein said textile material comprises at least one of a nonwoven web and a woven web.
6. The method of claim 1 , wherein said continuous coating is moisture vapor permeable.
7. The method of claim 5 , wherein said continuous coating is moisture vapor permeable.
8. The method of claim 1 , wherein said molten thermoplastic composition is at a temperature of less than about 160° C. when dispensed from the coating device.
9. A method of coating a thermoplastic composition on a substrate, said method comprising:
a) dispensing a molten thermoplastic composition having a complex viscosity of less than about 500 poise at about 1000 radians/second at a temperature of no greater than about 160° and a complex viscosity ranging from about 100 poise to about 1,000 poise at about 1 radian/second at a temperature of no greater than about 160° C., from a coating device in the form of a continuous film;
b) suspending the continuous film between the coating device and the substrate; and
c) contacting the substrate with said continuous film such that the angle defined by the substrate and the film is less than about 60 degrees,
said continuous film forming a continuous coating on said substrate.
10. The method of claim 9 , wherein said continuous film is adhered to said substrate.
11. The method of claim 9 , wherein said thermoplastic composition comprises a hot melt adhesive composition comprising thermoplastic polymer, tackifying resin, and plasticizer.
12. The method of claim 11 , wherein said hot melt adhesive composition comprises
no greater than 40% by weight said thermoplastic polymer,
no greater than 70% by weight said tackifying resin, and
no greater than 40% by weight said plasticizer.
13. The method of claim 9 , wherein said substrate comprises a textile material.
14. The method of claim 9 , wherein said coating device comprises a slot nozzle.
15. The method of claim 9 , wherein said continuous film is tacky.
16. The method of claim 9 , wherein the distance between the coating device and the substrate is at least about 0.5 mm.
17. The method of claim 9 , wherein the continuous film is coated on the substrate at a coat weight no greater than about 30 g/m 2 .
18. The method of claim 9 , wherein the continuous film is coated on the substrate at a coat weight no greater than about 10 g/m 2 .
19. The method of claim 9 , further comprising nipping said coated substrate between a first roller and a second roller.
20. The method of claim 9 , wherein said thermoplastic composition comprises at least one of ethylene-vinyl acetate, ethylene-methacrylate, synthetic rubber, and atactic polyolefin.
21. The method of claim 9 , wherein said molten thermoplastic composition is at a temperature of less than about 160° C. when dispensed from the coating device.