High temperature polyamide coating for fasteners
A high temperature polyamide coating and a fastener coated with a composition that includes from about 60 wt. % to about 80 wt. % of an aliphatic polyamide having a repeating unit. The composition also includes from about 3 wt. % to about 9 wt. % of an epoxy based resin having a molecular weight in the range from about 525 to about 585, from about 4 wt. % to about 10 wt. % of a ceramic microsphere material and from about 2 wt. % to about 5 wt. % of a thermoplastic methacrylate binder, from about 4 wt. % to about 12 wt. % of crushed glass, from about 0.1 wt. % to about 1 wt. % of a polyamide with a secondary amino group as a curing agent, and the balance of an epoxy based curing agent.
1. A high temperature polyamide composition comprising:
(a) from about 60 to about 80 percent by weight of an aliphatic polyamide;
(b) from about 3 to about 9 percent by weight of an epoxy based resin having a molecular weight in the range of about 525 to about 585;
(c) from about 4 to about 10 percent by weight of a ceramic microsphere material;
(d) from about 2 to about 5 percent by weight of a methacrylate based binder;
(e) from about 4 to about 12 percent by weight of a crushed glass material;
(f) from about 0.1 to about 1 percent by weight of an aliphatic amine curing agent; and
(g) the balance comprised of a curing agent for the epoxy based resin.
2. The high temperature polyamide composition as set forth in claim 1 wherein said methacrylate based binder is selected from the group consisting of poly(benzyl methacrylate), poly(butyl methacrylate), poly(cyclohexyl methacrylate), poly(ethyl methacrylate), poly(hexyl methacrylate), poly(isobutyl methacrylate), poly(isopropyl methacrylate), poly(methyl methacrylate), poly(phenyl methacrylate), poly(propyl methacrylate), and mixtures thereof.
3. The high temperature polyamide composition as set forth in claim 2 wherein said methacrylate based binder is poly(methyl methacrylate).
4. The high temperature polyamide composition as set forth in claim 1 wherein said aliphatic polyamide is selected from the group consisting of polyamide 11.
5. The high temperature polyamide composition as set forth in claim 1 wherein said epoxy based resin is selected from the group consisting of Bisphenol A Epoxy.
6. The high temperature polyamide composition as set forth in claim 1 wherein said ceramic micro-sphere material has micro-spheres with a diameter of about 40 microns.
7. The high temperature polyamide composition as set forth in claim 1 wherein the temperature is in the range of from about −54° C. (−65° F.) to about 250° C. (482° F.).
8. The high temperature polyamide composition as set forth in claim 1 wherein said crushed glass material is comprised of particles having a size of 70 microns.
9. The high temperature polyamide composition as set forth in claim 1 wherein said composition is resistant to degradation in properties up to 482° F.
10. A high temperature nylon coating for a fastener comprising:
(a) 73.90% by weight of an aliphatic polyamide;
(b) 7.66% by weight of a ceramic microsphere material;
(c) 8.72% by weight of a crushed glass material;
(d) 3.29% by weight of a poly (methyl methacrylate) binder;
(e) 5.51% by weight of a thermoplastic epoxy based resin material;
(f) 0.55% by weight of an aliphatic amine curing agent; and
(g) the balance of a curing agent for the epoxy based resin material.
11. The high temperature nylon coating as set forth in claim 10 wherein said aliphatic polyamide is Nylon 11.
12. The high temperature nylon coating as set forth in claim 10 wherein said ceramic micro-sphere is Zeeosphere® G-600.
13. The high temperature nylon coating as set forth in claim 10 wherein said poly (methyl methacrylate) is Degalan® LP 64/12.
14. The high temperature nylon coating as set forth, in claim 10 wherein said thermoplastic epoxy resin coating material is Epon® 1001F.
15. The high temperature nylon coating as set forth in claim 10 wherein said aliphatic polyamine based amine curing agent is Ancamine® 2014 AS.
16. The high temperature nylon coating as set forth in claim 10 wherein said curing agent for the epoxy based resin material is Curezol® 2MZ.
17. The high temperature nylon coating as set forth in claim 10 wherein said formula is resistant to degradation in properties up to 482° F.