Dense, shaped articles constructed of a refractory material and methods of preparing such articles
View Patent ↗The invention provides a method of forming a dense, shaped article, such as a crucible, formed of a refractory material, the method comprising the steps of placing a refractory material having a melting point of at least about 2900° C. in a mold configured to form the powder into an approximation of the desired shape. The mold containing the powder is treated at a temperature and pressure sufficient to form a shape-sustaining molded powder that conforms to the shape of the mold, wherein the treating step involves sintering or isostatic pressing. The shape-sustaining molded powder can be machined into the final desired shap and then sintered at a temperature and for a time sufficient to produce a dense, shaped article having a density of greater than about 90% and very low open porosity. Preferred refractory materials include tantalum carbide and niobium carbide.
1. A method of forming a dense, shaped article formed of a refractory material, comprising;
providing a refractory material powder having a melting point of at least about 2900° C., the refractory material powder consisting of a refractory material selected from the group consisting of carbides of tantalum, niobium or hafnium, nitrides of tantalum, niobium or hafnium, and alloys or powder mixtures thereof;
placing the refractory material powder in a mold configured to form the powder into a desired shape;
treating the mold containing the powder at a temperature and pressure sufficient to form a self-supporting and shape-sustaining molded powder that conforms to the shape of the mold, wherein said treating step comprises applying an isostatic or uni-axial pressure;
machining the shape-sustaining molded powder to further shape the molded powder; and
sintering the shape-sustaining molded powder in an inert atmosphere at a pressure ranging from vacuum to about 10 atm and at a temperature and for a time sufficient to produce a dense shaped article having a density greater than about 90%, a total porosity of no more than about 10%, and a total open porosity of no more than about 1%.
2. The method of claim 1 , wherein said treating step comprises sintering the powder contained within the mold at a temperature of about 1000 to about 2000° C. while concurrently applying a uni-axial pressure of at least about 50 MPa.
3. The method of claim 2 , wherein said treating step comprises sintering the powder contained within the mold at a temperature of about 1500 to about 1700° C. while concurrently applying a uni-axial pressure of at least about 100 MPa.
4. The method of claim 1 , wherein said treating step comprises isostatically pressing the powder contained within the mold at a pressure of about 50 to about 500 MPa and at about room temperature.
5. The method of claim 1 , wherein said sintering step comprises sintering the shape-sustaining molded powder at a temperature of about 2100 to about 2500° C.
6. The method of claim 1 , wherein said sintering step comprises sintering the shape-sustaining molded powder at a maximum sintering temperature for about 10 to about 50 hours, with a temperature ramp-up period of about 5 to about 20 hours during which the sintering temperature is raised about 100 to about 400° C. per hour, and a cool down period of about 5 to about 20 hours during which the sintering temperature is decreased about 100 to about 400° C. per hour.
7. The method of claim 1 , wherein the shape-sustaining molded powder has a density of about 60 to about 80%.
8. The method of claim 1 , wherein the dense, shaped article has a density greater than about 95%, a total porosity of no more than about 5%, and a total open porosity of no more than about 0.5%.
9. The method of claim 1 , wherein the dense, shaped article has a density greater than about 97%, a total porosity of no more than 3%, and a total open porosity of no more than about 0.25%.
10. The method of claim 1 , wherein the mold is adapted for forming the refractory material into the shape of a crucible.
11. The method of claim 1 , wherein the refractory material powder consists of a tantalum carbide powder.
12. The method of claim 1 , wherein the refractory material powder has a melting point of at least about 3200° C.
13. The method of claim 1 , wherein the refractory material powder has a melting point of at least about 3600° C.
14. A method of forming a dense, shaped, tantalum carbide article, comprising;
providing a refractory material powder consisting of tantalum carbide;
placing the powder in a mold configured to form the powder into a desired shape;
sintering the powder contained within the mold in an inert atmosphere or under a vacuum and at a temperature of at least about 1500° C., while concurrently applying a uni-axial pressure of at least about 50 MPa, to form a self-supporting and shape-sustaining molded tantalum carbide powder that conforms to the shape of the mold, the molded powder having a density of about 60 to about 80%;
machining the shape-sustaining molded tantalum carbide powder to further shape the molded powder; and
sintering the shape-sustaining molded tantalum carbide powder in an inert atmosphere at a temperature of about 2100 to about 2500° C. and a pressure ranging from vacuum to about 10 atm for a time sufficient to produce a dense, shaped, tantalum carbide article having a density greater than about 95%, a total porosity of no more than about 5%, and a total open porosity of no more than about 0.5%.
15. The method of claim 14 , wherein said treating step comprises sintering the powder at a temperature of about 1500 to about 1700° C. and applying a uni-axial pressure of at least about 100 MPa.
16. The method of claim 14 , wherein said sintering step comprises sintering the shape-sustaining molded powder at a maximum sintering temperature for about 10 to about 50 hours, with a temperature ramp-up period of about 5 to about 20 hours during which the sintering temperature is raised about 100 to about 400° C. per hour, and a cool down period of about 5 to about 20 hours during which the sintering temperature is decreased about 100 to about 400° C. per hour.
17. The method of claim 14 , wherein the dense, shaped article has a density greater than about 97%, a total porosity of no more than 3%, and a total open porosity of no more than about 0.25%.
18. A method of forming a dense, shaped article formed of a refractory material, comprising;
providing a refractory material powder consisting of a refractory material selected from the group consisting of carbides of tantalum, niobium or hafnium, nitrides of tantalum, niobium or hafnium, and alloys or powder mixtures thereof;
placing the refractory material powder in a mold configured to form the powder into a desired shape;
treating the powder at a temperature and pressure sufficient to form a self-supporting and shape-sustaining molded powder that conforms to the shape of the mold and has a density of about 60% to about 80% of theoretical density, wherein said treating step comprises applying an isostatic pressure of about 50 to about 500 MPa or a uni-axial pressure of least about 50 MPa;
machining the shape-sustaining molded powder to further shape the molded powder; and
sintering the shape-sustaining molded powder in an inert atmosphere at a pressure ranging from vacuum to about 10 atm, wherein said sintering step comprises heating the shape-sustaining molded powder into a range of about 2100° C. to about 2500° C., and wherein said sintering step continues for a time sufficient to produce a dense shaped article having a density greater than about 95%, a total porosity of no more than about 5%, and a total open porosity of no more than about 0.5%.
19. The method of claim 18 , wherein said treating step comprises sintering the powder in an inert atmosphere or under a vacuum and at a temperature of at least about 1500° C.
20. The method of claim 18 , wherein said treating step comprises sintering the powder at a temperature of about 1500 to about 1700° C. and applying a uni-axial pressure of at least about 100 MPa.
21. The method of claim 18 , wherein said sintering step comprises sintering the shape-sustaining molded powder at a maximum sintering temperature for about 10 to about 50 hours, with a temperature ramp-up period of about 5 to about 20 hours during which the sintering temperature is raised about 100 to about 400° C. per hour, and a cool down period of about 5 to about 20 hours during which the sintering temperature is decreased about 100 to about 400° C. per hour.
22. The method of claim 18 , wherein the dense, shaped article has a density greater than about 97%, a total porosity of no more than 3%, and a total open porosity of no more than about 0.25%.
23. The method of claim 18 , wherein the refractory material powder consists of a tantalum carbide powder.