Hydrophobic sand treated with wax blend
View Patent ↗A method for making hydrophobic sand including coating sand with a wax blend so as to form a coated sand with advanced hydrophobic properties, wherein a weight ratio of the wax blend to total coated sand weight is about 0.05%–10%, and the wax blend includes a weight ratio of about 50.01% to 99.99% of a main wax, and about 49.99% to 0.01% of a secondary wax.
1. A method for making hydrophobic sand comprising:
coating sand with a wax blend so as to form an at least partially coated sand with advanced hydrophobic properties, wherein a weight ratio of the wax blend to total coated sand weight is about 0.05%–10%, and the wax blend includes a weight ratio of about 50.01% to 99.99% of a main wax, and about 49.99% to 0.01% of a secondary wax, wherein the at least partially coated sand is a free flowing material and the wax blend is not a binder that fuses the sand from being free flowing.
2. The method according to claim 1 , wherein the wax blend includes a weight ratio of about 75% to 99% of the main wax, and about 25% to 1% of the secondary wax.
3. The method according to claim 1 , wherein the wax blend includes a weight ratio of about 85%–98% of the main wax, and about 2–15% of the secondary wax.
4. The method according to claim 1 , wherein said main wax comprises a soft macro-crystalline wax with a congealing point of about 10–45° C.
5. The method according to claim 1 , wherein said main wax comprises a hard macro-crystalline wax with a congealing point of about 40–85° C.
6. The method according to claim 1 , wherein said main wax comprises at least one of paraffin wax, bee wax, carnauba wax, candelila wax, bayberry wax, Japan wax, Fischer-Tropsch process wax, polyethylene wax, polypropylene wax, bitumen, and tar.
7. The method according to claim 1 , wherein said secondary wax comprises a microcrystalline wax with a congealing point higher than about 70° C.
8. The method according to claim 7 , wherein said secondary wax comprises a microcrystalline wax with a congealing point at least 10° C. higher than that of the main wax.
9. The method according to claim 1 , wherein said secondary wax comprises montan wax with a congealing point higher than 70° C.
10. The method according to claim 1 , wherein said secondary wax comprises at least one of peat wax, castor wax, jojoba wax, a paraffin precipitation process wax, Fischer-Tropsch process wax, polyethylene wax, and polypropylene wax.
11. The method according to claim 1 , wherein said wax blend comprises at least one of an emulsion, a suspension, a solution, a dispersion, a hot melt, and solid form.
12. An article comprising sand at least partially coated with a wax blend so as to form an at least partially coated sand with advanced hydrophobic properties, wherein a weight ratio of the wax blend to total coated sand weight is about 0.05%–10%, and the wax blend includes a weight ratio of about 50.01% to 99.99% of a main wax, and about 49.99% to 0.01% of a secondary wax, wherein the at least partially coated sand is a free flowing material and the wax blend is not a binder that fuses the sand from being free flowing.