View Patent ↗A process for the copolymerization of ethylene and α-olefins which utilizes a mixed modifier comprised of a conjugated diene and alkoxysilane is disclosed.
1. In a process for the copolymerization of ethylene with a C 3-8 α-olefin comonomer utilizing a transition metal-containing catalyst and organoaluminum cocatalyst, to modify short-chain branching characteristics, the improvement comprising conducting the copolymerization in an inert hydrocarbon medium in the presence of a mixed modifier comprised of a conjugated diene containing 4 to 12 carbon atoms and an alkoxysilane of the formula R′ 4-y Si(OR) y where y is 2 or 3, R is an alkyl group having from 1 to 10 carbon atoms and R′ is a C 1-10 alkyl or C 6-10 aryl group; said conjugated diene present in an amount from about 100 to 5000 ppm based on the weight of the hydrocarbon and said alkoxysilane present in an amount from about 1 to 50 ppm based on the weight of the hydrocarbon.
2. The process of claim 1 wherein the conjugated diene is selected from the group consisting of 1,3-butadiene, 1,3-pentadiene, 1,3-hexadiene and 2-methyl-1,3-butadiene.
3. The process of claim 1 wherein R and R′ of the alkoxysilane are C 1-6 linear or cyclic alkyl groups.
4. The process of claim 3 wherein the alkoxysilane is a monoalkyltrialkoxysilane or dialkyldialkoxysilane.
5. The process of claim 4 wherein the alkoxysilane is cyclohexylmethyldimethoxysilane.
6. The process of claim 4 wherein the alkoxysilane is methyltriethoxysilane.
7. The process of claim 1 wherein the conjugated diene is present in an amount from about 250 to 4000 ppmw and the alkoxysilane is present in an amount from about 2.5 to 40 ppmw.
8. The process of claim 1 wherein the copolymerization is conducted as one stage of a multi-stage polymerization process.
9. The process of claim 8 wherein the polymerization stages are conducted in series.
10. The process of claim 9 wherein ethylene is homopolymerized in a first stage and homopolymer produced therein fed to a second stage where the copolymerization is conducted in the presence of said homopolymer and mixed modifier.
11. The process of claim 9 wherein ethylene is copolymerized in a first stage and copolymer produced therein fed to a second stage where further copolymerization is conducted in the presence of said copolymer and mixed modifier.
12. The process of claim 8 wherein the polymerization stages are conducted in parallel.