Ferromagnetic nanoparticles, material coated with dispersion of ferromagnetic nanoparticles, and magnetic recording medium using the material
View Patent ↗Ferromagnetic nanoparticles which are produced by reducing, in the presence of a polymer, two or more metals having different reduction potentials twice or more, using two or more reducing agents having different reduction potentials, a material coated with a dispersion of ferromagnetic nanoparticles in which the ferromagnetic nanoparticles are dispersed, and a magnetic recording medium which has a magnetic layer consisting of the material. The ferromagnetic nanoparticles having a holding power Hc of 95.5 kA/m or more, the material coated with the dispersion of ferromagnetic nanoparticles having excellent industrial coatability, and the magnetic recording medium using the dispersion are provided.
1. A method for producing ferromagnetic nanoparticles comprising:
reducing, in the presence of a polymer, at least two metals having different reduction potentials at least twice, using at least two reducing agents having different reduction potentials to obtain a resultant mixture, and
heating the resultant,
wherein at least two of the metals are a noble metal and a poor metal, the noble metal is reduced before the poor metal, the ferromagnetic nanoparticles are ferromagnetic regular alloys having a CuAu or Cu 3 Au crystal structure, and a particle size of the ferromagnetic nanoparticles is 3 to 20 nm.
2. The method according to claim 1 , wherein the heating is conducted by using a laser.
3. The method according to claim 2 , wherein the method further comprises oxidizing the resultant before the heating, and wherein the heating is conducted under a non-oxidative atmosphere.
4. The-method according to claim 3 , wherein the noble metal is reduced with a reducing agent having a reduction potential higher than −0.2 V and the poor metal is reduced with a reducing agent having a reduction potential lower than −0.2 V.
5. The method according to claim 3 , wherein the noble metal is platinum and the poor metal is iron.
6. The method according to claim 2 , wherein the noble metal is reduced with a reducing agent having a reduction potential higher than −0.2 V and the poor metal is reduced with a reducing agent having a reduction potential lower than −0.2 V.
7. The method according to claim 2 , wherein the noble metal is platinum and the poor metal is iron.
8. The method according to claim 2 , wherein the heating is conducted under an N 2 atmosphere and the laser is an Ar laser.
9. The method according to claim 1 , wherein the method further comprises oxidizing the resultant before the heating, and wherein the heating is conducted under a non-oxidative atmosphere.
10. The method according to claim 9 , wherein the noble metal is reduced with a reducing agent having a reduction potential higher than −0.2 V and the poor metal is reduced with a reducing agent having a reduction potential lower than −0.2 V.
11. The method according to claim 9 , wherein the noble metal is platinum and the poor metal is iron.
12. The method according to claim 1 , wherein the noble metal is reduced with a reducing agent having a reduction potential higher than −0.2 V and the poor metal is reduced with a reducing agent having a reduction potential lower than −0.2 V.
13. The method according to claim 1 , wherein at least one of the metals is selected from the group consisting of Co, Fe, Ni, Mn, Cr, Pr, Pt, Au, Ag, Ir, and Rh.
14. The method according to claim 1 , wherein the noble metal is platinum and the poor metal is iron.
15. The method according to claim 1 , wherein the particle size of the ferromagnetic nanoparticles is 3 to 10 nm.