Aluminum alloys for armored cables
View Patent ↗Disclosed is an armored electrical or optical cable that includes at least one flexible elongated conducting member for conducting electrical or optical signals and an armor layer surrounding the conducting member, the armor layer including a 5xxx aluminum alloy having greater than 3 wt. % Mg. Such aluminum alloys include, e.g., 5182. Other alternative alloys are disclosed. In one embodiment, the aluminum alloy material is a 5xxx alloy material having an elongation that is 8% or greater, a tensile yield strength that is 207 MPa (30 ksi) or greater, and an ultimate tensile strength that is 276 MPa (40 ksi) or greater. The disclosed armor layer provides substantial weight reduction and cost benefits over steel cable armor, is more environmentally friendly than steel, and has physical properties that are comparable to or better than that of steel.
1. A cable, comprising:
at least one flexible elongated conducting member for conducting electrical or optical signals;
an armor layer surrounding said conducting member,
wherein the armor layer is formed as a longitudinally rolled and seamed tubular layer,
wherein the armor layer is corrugated,
the armor layer comprising a 5xxx aluminum alloy having greater than 3 wt. % Mg, wherein the aluminum alloy has been treated to a temper, which is one of H1X, H2X and H3X;
the armor layer having a thickness less than 0.3 mm (0.012-in.).
2. The armored cable in accordance with claim 1 , wherein said 5xxx aluminum alloy comprises a 5182 alloy.
3. The armored cable in accordance with claim 1 , wherein said 5xxx aluminum alloy comprises a 5154 alloy.
4. The armored cable in accordance with claim 1 , wherein said 5xxx aluminum alloy comprises a 5254 alloy.
5. The armored cable in accordance with claim 1 , wherein said aluminum alloy is partial annealed to an H25, H26, or H28 temper.
6. The armored cable in accordance with claim 1 , wherein said armor layer is bare.
7. The armored cable in accordance with claim 1 , wherein said armor layer is coated with ethylene acrylic acid.
8. The armored cable in accordance with claim 1 , wherein said conducting member is an optical fiber.
9. The armored cable in accordance with claim 1 , wherein said conducting member is an electrical conductor.
10. The armored cable in accordance with claim 1 , further comprising at least one inner jacket between said armor layer and said conducting member.
11. The armored cable in accordance with claim 1 , further comprising at least one outer jacket surrounding said armor layer.
12. The armored cable in accordance with claim 1 , wherein said 5xxx aluminum alloy comprises a 5042 alloy.
13. A cable, comprising:
at least one elongated conducting member for conducting electrical or optical signals;
an armor layer surrounding said conducting member,
wherein the armor layer is formed as a longitudinally rolled and seamed tubular layer,
wherein the armor layer is corrugated, the armor layer comprising an aluminum alloy selected from the group consisting of:
aluminum alloys having an Aluminum Association designation of 5042,
aluminum alloys having an Aluminum Association designation of 5182,
aluminum alloys having an Aluminum Association designation of 5154,
and aluminum alloys having an Aluminum Association designation of 5254, wherein the aluminum alloy has been treated to a temper, which is one of H1X, H2X and H3X;
the armor layer having a thickness less than 0.3 mm (0.012-in.).
14. The armored cable in accordance with claim 13 , wherein said aluminum alloy is partial annealed to an H25, H26, or H28temper.
15. The armored cable in accordance with claim 13 , wherein said conducting member is an optical fiber.
16. The armored cable in accordance with claim 13 , wherein said conducting member is an electrical conductor.
17. The armored cable in accordance with claim 13 , further comprising at least one inner jacket between said armor layer and said conducting member.
18. The armored cable in accordance with claim 13 , further comprising at least one outer jacket surrounding said armor layer.
19. The armored cable in accordance with claim 13 , wherein said armor layer is corrugated.
20. The armored cable according to claim 13 , wherein the armor layer has a thickness between 0.08 mm (0.003 in.) and 0.3 mm (0.012 in.).
21. A cable, comprising:
at least one elongated conducting member for conducting electrical or optical signals;
an armor layer surrounding said conducting member,
wherein the armor layer is formed as a longitudinally rolled and seamed tubular layer,
wherein the armor layer is corrugated, the armor layer comprising an aluminum alloy selected from the group consisting of:
aluminum alloys having an Aluminum Association designation of 5042, aluminum alloys having an Aluminum Association designation of 5182, aluminum alloys having an Aluminum Association designation of 5154, and aluminum alloys having an Aluminum Association designation of 5254, wherein the aluminum alloy has been treated to a temper, which is one of H1X, H2X and H3X;
wherein said armor layer is coated with ethylene acrylic acid.
22. A cable, comprising:
at least one flexible elongated conducting member for conducting electrical or optical signals;
an armor layer surrounding said conducting member,
wherein the armor layer is formed as a longitudinally rolled and seamed tubular layer,
wherein the armor layer is corrugated,
the armor layer comprising a 5xxx aluminum alloy material having an elongation that is 10% or greater,
a tensile yield strength that is 207 MPa (30 ksi) or greater, and
an ultimate tensile strength of 276 MPa (40 ksi) or greater, wherein the aluminum alloy has been treated to a temper, which is one of H1X, H2X and H3X;
the armor layer having a thickness less than 0.3 mm (0.012-in.).
23. The armored cable in accordance with claim 22 , wherein said aluminum alloy material has an elongation that is 10% or greater.
24. The armored cable in accordance with claim 22 , wherein said aluminum alloy material has a tensile yield strength that is 193 MPa (28 ksi) or greater.
25. The armored cable in accordance with claim 22 , wherein said aluminum alloy material has an ultimate tensile strength that is 262 MPa (38 ksi) or greater.