View Patent ↗Described are medical implant devices that include particulate collagen and particulate demineralized bone matrix. These and potentially other materials are held together in a three-dimensionally stable structure such as a porous, resilient sheet, by an ionically-crosslinked polysaccharide gel. Also described are methods for making and using such medical devices.
1. A demineralized bone matrix (DBM) device, comprising:
a three-dimensionally stable, porous implant structure, wherein said structure is a resilient, porous sheet material;
said three-dimensionally stable, porous implant structure comprising an admixture including particulate solids, said particulate solids including a particulate collagen material and a particulate DBM material in a weight ratio of 1:12 to about 1:2, respectively; and
said admixture including particulate solids retained in the form of said porous implant structure by an ionically-crosslinked polysaccharide gel, wherein said polysaccharide is an alginate.
2. The DBM device of claim 1 , wherein said porous implant structure is a lyophilized material.
3. The DBM device of claim 1 , wherein said structure is comprised about 20% to about 80% by weight of said DBM material on a dry weight basis.
4. The DBM device of claim 1 , wherein said structure is comprised about 5% to about 30% by weight of said collagen material on a dry weight basis.
5. The DBM device of claim 1 , wherein said structure is comprised about 5% to about 20% by weight of said polysaccharide on a dry weight basis.
6. The DBM device of claim 1 , wherein said particulate collagen material comprises particulated collagen sponge.
7. The DBM device of claim 1 , wherein said gel is hydrated with an aqueous liquid medium.
8. The DBM device of claim 1 , wherein said gel is ionically crosslinked with a calcium salt.
9. The DBM device of claim 8 , wherein said calcium salt is calcium chloride.
10. The DBM device of claim 1 , prepared by a process that comprises:
forming an admixture including water, said polysaccharide, wherein said polysaccharide is an alginate, said particulate collagen material, and said particulate DBM material;
contacting said admixture with a liquid medium containing an amount of a multivalent ionic agent effective to ionically crosslink said polysaccharide and obtain an ionically-crosslinked wet precursor material having said particulate collagen material and said particulate DBM material entrained therein;
freezing said ionically-crosslinked wet precursor material to form a frozen precursor material; and
drying said frozen precursor material.
11. The DBM device of claim 1 , wherein said DBM material retained in said porous implant structure exhibits osteoinductivity.
12. The DBM device of claim 1 , wherein said particulate DBM material is osteoinductive, and wherein said particulate solids are bound in said resilient, porous sheet material in the absence of covalent chemical crosslinking of particles of the particulate solids to one another.