Cathode active material, method of manufacturing it, cathode, and battery
View Patent ↗A cathode active material capable of increasing a capacity and improving high temperature characteristics or cycle characteristics, a method of manufacturing it, a cathode using the cathode active material, and a battery using the cathode active material are provided. In a cathode active material contained in a cathode, a coating layer is provided on at least part of a complex oxide particle containing at least lithium (Li) and cobalt (Co). The coating layer is an oxide which contains lithium (Li) and at least one of nickel (Ni) and manganese (Mn).
1. A cathode active material comprising more than one complex oxide particle, each complex oxide particle made of:
an oxide particle core containing at least lithium (Li) and cobalt (Co); and
a coating layer on at least part of the oxide particle core,
wherein,
the coating layer is made of an oxide containing lithium and at least nickel and manganese,
a concentration of manganese in an outer portion of the coating layer is higher than that in an inner portion of the coating layer,
a concentration of nickel in an outer portion of the coating layer is higher than that in an inner portion of the coating layer, and
the amount of the coating layer is 0.5 wt% to 50 wt% of the complex oxide particle.
2. The cathode active material according to claim 1 , wherein the composition of the oxide particle core is expressed by Chemical formula 1:
Li (1+w) Co (1−x−y) M1 x M2 y O (2−z),
where,
M1 represents at least one selected from the group consisting of magnesium (Mg), aluminum (Al), titanium (Ti), and zirconium (Zr),
M2 represents at least one selected from the group consisting of boron (B), vanadium (V), chromium (Cr), manganese (Mn), iron (Fe), nickel (Ni), copper (Cu), zinc (Zn), molybdenum (Mo), tin (Sn), tungsten (W), yttrium (Y), niobium (Nb), calcium (Ca), and strontium (Sr), and
each of w, x, y, and z are respectively in the range of −0.10 ≦w≦0.10, 0.001<x<0.10, 0≦y<0.40, and −0.10≦z≦0.20.
3. The cathode active material according to claim 1 , wherein:
(a) the composition of the oxide particle core is expressed by Chemical formula 2, and
(b) Chemical formula 2 is:
Li (1+x) Co (1−y) M y O (2−z),
where M represents at least one selected from the group consisting of magnesium (Mg), aluminum (Al), boron (B), titanium (Ti), vanadium (V), chromium (Cr), manganese (Mn), iron (Fe), nickel (Ni), copper (Cu), zinc (Zn), molybdenum (Mo), tin (Sn), tungsten (W), zirconium (Zr), yttrium (Y), niobium (Nb), calcium (Ca), and strontium (Sr), and
each of x, y, and z respectively are in the range of −0.10≦x≦0.10, 0≦y<0.50, and −0.10≦z≦0.20.
4. The cathode active material according to claim 3 , wherein the mole ratio of nickel to manganese in the coating layer is in the range from 90:10 to 30:70.
5. The cathode active material according to claim 1 , wherein:
(a) the composition of the oxide particle core is expressed by Chemical formula 3,
(b) in diffraction peaks obtained by CuKαpowder X-ray diffraction, there is a diffraction peak of the coating layer on the lower angle side in the range from 0.2 deg to 1.0 deg than diffraction angle 2θ of a diffraction peak belonging to face [ 101 ] of the complex oxide particle, and
(c) Chemical formula 3 is:
Li (1+x) Co (1−y) M y O (2−z),
where, M represents at least one selected from the group consisting of magnesium (Mg), aluminum (Al), boron (B), titanium (Ti), vanadium (V), chromium (Cr), manganese (Mn), iron (Fe), nickel (Ni), copper (Cu), zinc (Zn), molybdenum (Mo), tin (Sn), tungsten (W), zirconium (Zr), yttrium (Y), niobium (Nb), calcium (Ca), and strontium (Sr), and
each of x, y, and z are respectively in the range of −0.10≦x≦0.10, 0≦y<0.50, and −0.10≦z≦0.20.
6. The cathode active material according to claim 5 , wherein the composition ratio between nickel and manganese in the coating layer to a mole ratio of nickel: manganese is in the range from 90:10 to 30:70.
7. The cathode active material according to claim 1 , wherein the oxide of the coating layer further contains at least one selected from the group consisting of cobalt (Co), magnesium, aluminum, titanium, zirconium, boron, vanadium, chromium, iron, copper, zinc, molybdenum, tin, tungsten, yttrium, niobium, calcium, and strontium.
8. The cathode active material according to claim 1 , wherein the average particle diameter of the complex oxide particle is in the range from 2.0 μm to 50 μm.