Method for making alkylated phenols
View Patent ↗An alkylation method comprises reacting a hydroxy aromatic compound with an alkyl alcohol in the presence of an alkylation catalyst comprising a metal oxide wherein the alkylation catalyst, has a surface area to volume ratio of about 950 to about 4,000 m 2 /m 3 , an aspect ratio of about 0.7 to about 1.0 or a combination of the foregoing.
1. An alkylation method comprising reacting a hydroxy aromatic compound with an alkyl alcohol in the presence of an alkylation catalyst comprising a metal oxide wherein the alkylation catalyst has a surface area to volume ratio of about 950 to about 4,000 m 2 /m 3 , an aspect ratio of about 0.7 to about 1.0 or a combination of the foregoing, and further wherein the metal oxide comprises magnesium oxide, iron oxide, or a combination thereof.
2. The method of claim 1 , wherein the reacting takes place at a temperature of at least about 420° C.
3. The method of claim 1 , wherein the metal oxide comprises magnesium oxide, iron oxide or a combination of the foregoing.
4. The method of claim 1 , wherein the catalyst has pores with diameters of about 100 to about 400 Angstroms after calcination.
5. The method of claim 1 , wherein the catalyst has a bimodal distribution of pores.
6. The method of claim 1 , having a surface area to volume ratio of about 1100 to about 3800 m 2 /m 3 .
7. The method of claim 1 , wherein the catalyst is in the form of pellets having a diameter of about 1.0 to about 4.0 millimeters and a height of about 2.0 to about 3.0 millimeters.
8. The method of claim 1 , wherein the catalyst is in the form of pellets having a pellet density of about 1.3 to about 2.10 grams per cubic centimeter.
9. The method of claim 1 , wherein the hydroxy aromatic compound is phenol.
10. The method of claim 1 , wherein the hydroxy aromatic compound is o-cresol.
11. The method of claim 1 , wherein the alkyl alcohol is methyl alcohol.
12. The method of claim 1 , wherein reacting takes place at a temperature of about 440° C. to about 500° C.