Hydrothermally stable microporous molecular sieve catalyst and preparation method thereof
View Patent ↗Disclosed are a hydrothermally stable porous molecular sieve catalyst and a preparation method thereof. The catalyst consists of a product obtained by the evaporation of water from a raw material mixture comprising a molecular sieve having a framework of Si—OH—Al—, a water-insoluble metal salt and a phosphate compound. The catalyst maintains its physical and chemical stabilities even in an atmosphere of high temperature and humidity. Accordingly, the catalyst shows excellent catalytic activity even when it is used in a severe process environment of high temperature and humidity in heterogeneous catalytic reactions, such as various oxidation/reduction reactions, including catalytic cracking reactions, isomerization reactions, alkylation reactions and esterification reactions.
1. A hydrothermally stable porous molecular sieve catalyst, which consists of a product obtained by the evaporation of water from a raw material mixture comprising 100 parts by weight of a molecular sieve having a framework of —Si—OH—Al—, 0.0 1-5.0 parts by weight of a water-insoluble metal salt, and 0.05-17.0 parts by weight of a phosphate compound selected from a group consisting of phosphoric acid (H 3 PO 4 ), ammoniunm phosphate and alkyl phosphate; in which surface pores of the molecular sieve are modified with one of compounds represented by following formulas 1 to 3:
[Formula 1]
M x (H 2 PO 4 ) y , wherein M is a metal, x is 1, and y is an integer from 2 to 6;
[Formula 2]
M x (HPO 4 ) y , wherein M is a metal, x is 2, and y is an integer from 2 to 6; and
[Formula 3]
Mx(PO 4 ) y , wherein M is a metal, x is 3, and y is an integer from 2 to 6.
2. The catalyst of claim 1 , wherein a molar ratio of the water-insoluble metal salt to the phosphate compound is 1.0:0.3-10.0.
3. The catalyst of claim 1 , wherein the molecular sieve is a zeolite having a Si/Al molar ratio of 1-300 and a pore size of 4-10 Å, or a mesoporous molecular sieve having a pore size of 10-100 Å.
4. The catalyst of claim 3 , wherein the molecular sieve is selected from a group consisting of ZSM-5, Ferrierite, ZSM-11, Mordenite, Beta-zeolite, MCM-22, L-zeolite, MCM-41, SBA-15 and Y-zeolite.
5. The catalyst of claim 1 , wherein the water-insoluble metal salt is an oxide, hydroxide, carbonate or oxalate of at least one metal selected from a group consisting of alkaline earth metals, transition metals, and heavy metals having an oxidation state of +3 to +5.
6. A method for preparing a hydrothermally stable porous molecular sieve catalyst, the method comprising the steps of:
(a) mixing a phosphate compound selected from a group consisting of phosphoric acid, ammonium phosphate and alkyl phosphate, a water-insoluble salt and water with each other to prepare the aqueous slurry which has a raw material composition comprising 100 parts by weight of the molecular sieve, 0.01-5.0 parts by weight of the water-insoluble metal salt and 0.05-17.0 parts by weight of the phosphate compound;
(b) adjusting a pH of the slurry such that the phosphate compound in the slurry is present as an ion selected from among a monohydrogen phosphate ion ([HPO 4 ] 2− ), a dihydrogen phosphate ion ([H 2 PO 4 ] − ) and a phosphate ion ([PO 4 ] 3− ), and stirring the slurry;
(c) adding the molecular sieve having a framework of —Si—OH—Al— to the slurry of step (b); and
(d) removing water from the aqueous slurry by an evaporation process, followed by filtration to collect the solid product.
7. The method of claim 6 , wherein a molar ratio of the water-insoluble metal salt to the phosphate compound is 1.0:0.3-10.0.
8. The method of claim 6 , wherein the stirring in step (b) is carried out at a temperature of 20-60° C. for a period ranging from 30 minutes to 3 hours.
9. The method of claim 6 , wherein the evaporation process in step (d) is carried out at a temperature of 10-90° C.
10. The method of claim 6 , wherein the molecular sieve is a zeolite having a Si/Al molar ratio of 1-300 and a pore size of 4-10 Å, or a mesoporous molecular sieve having a pore size of 10-100 Å.
11. The method of claim 10 , wherein the molecular sieve is selected from a group consisting of ZSM-5, Ferrierite, ZSM-11, Mordenite, Beta-zeolite, MCM-22, L-zeolite, MCM-41, SBA-15 and Y-zeolite.
12. The catalyst of claim 6 , wherein the water-insoluble metal salt is an oxide, hydroxide or carbonate of at least one metal selected from a group consisting of alkaline earth metals, transition metals, and heavy metals having an oxidation state from +3 to +5.
13. A method for preparing a hydrothermally stable porous molecular sieve catalyst, the method comprising the steps of:
(a) mixing a phosphate compound selected from a group consisting of phosphoric acid, ammonium phosphate and alkyl phosphate, the water-insoluble metal salt and water with each other to prepare the aqueous slurry;
(b) adjusting a pH of the mixture such that the phosphate compound in a resultant mixture is present as an ion selected from a monohydrogen phosphate ion, a dihydrogen phosphate ion and a phosphate ion, and stirring the mixture
(c) removing water from the aqueous slurry through a first evaporation process, followed by filtration to collect a first solid product;
(d) preparing an aqueous slurry containing a molecular sieve having a framework of —Si—OH—Al—; and
(e) adding the first solid product to the molecular sieve-containing aqueous slurry, and removing water from a resultant mixture solution through a second evaporation process, followed by filtration to separate a second solid product;
in which the phosphate compound and the water-insoluble metal salt are used in amounts of 0.05-17.0 parts by weight and 0.0 1-5.0 parts by weight, respectively, based on 100 parts by weight of the molecular sieve.
14. The method of claim 13 , wherein a molar ratio of the water-insoluble metal salt to the phosphate compound is 1.0:0.3-10.0.
15. The method of claim 13 , wherein the first solid product is added in an amount of 0.01-20.0 parts by weight, based on 100 parts by weight of the molecular sieve.
16. The method of claim 13 , wherein mixing in step (b) is carried out at a temperature of 20-60° C. for a period ranging from 30 minutes to 3 hours.
17. The method of claim 13 , wherein the first evaporation process is carried out at a temperature of 10-90° C.
18. The method of claim 13 , wherein the second evaporation process is carried out at a temperature of 20-60° C.
19. The method of claim 13 , wherein the molecular sieve is a zeolite having a Si/Al molar ratio of 1-300 and a pore size of 4-10 Å, or a mesoporous molecular sieve having a pore size of 10-100 Å.
20. The method of claim 13 , wherein the water-insoluble metal salt is an oxide, hydroxide or carbonate of at least one metal selected from a group consisting of alkaline earth metals, transition metals, and heavy metals having an oxidation state from +3 to +5.