Materials leading to improved dental composites and dental composites made therefrom
View Patent ↗This invention relates to composite materials for restorative dentistry. More particularly, it relates to new components for dental composites, which impart an attractive combination of good mechanical properties and low shrinkage.
1. An uncured dental composite material comprising
a. a composition comprising at least one compound of the formula:
E 1 -R 1 n —O—R 2 -Q-R 3 —O—R 4 m -E 2
wherein:
Q is selected from the group consisting of:
(i) a carbocyclic ring containing 5 or 6 carbon atoms with up to 3 C 1-3 alkyl substituents on the ring;
(ii) S—R 5 -T wherein S and T are each independently carbocyclic rings containing 5 or 6 carbon atoms with up to 3 C 1-3 alkyl substituents on the ring, and R 5 is a covalent bond or an alkylene group containing 1, 2, 3 or 4 carbon atoms; and
(iii) a carbocyclic fused ring system containing two fused rings containing a total of 8 to 10 carbon atoms with up to 4 C 1-3 alkyl substituents on the fused ring system;
R 2 and R 3 are each independently selected from the group consisting of a covalent bond and an alkylene group containing 1 to 4 carbon atoms;
R 1 is a repeat unit of the formula
R 4 is a repeat unit of the formula
E 1 and E 2 are each independently
wherein R 6 is H (acryloyl) or CH 3 (methacryloyl);
n and m are each independently an integer greater than 0;
a is independently an integer from 3 to 6;
a′ is independently an integer from 3 to 6;
provided that neither R 2 nor R 3 is a covalent bond bonded directly to an aromatic ring;
and provided that the degree of polymerization of the at least one compound is between 2 and 30;
b. optionally, at least one other polymerizable (meth)acrylic ester component;
c. at least one polymerization initiator compound; and
d. at least one filler selected from the group consisting of barium aluminum silicate, barium aluminum borosilicate, ytterbium trifluoride, glass beads, silica, quartz, borosilicates, alumina, alumina silicates, and mixtures thereof, wherein the total amount of the at least one filler is from about 40 weight percent to about 90 weight percent, based on the total weight of the uncured dental composite material.
2. The uncured dental composite material of claim 1 wherein Q is selected from the group consisting of
3. The uncured dental composite material of claim 2 wherein Q is 1,4-cyclohexylene.
4. The uncured dental composite material of claim 1 wherein Q is S—R 5 -T, R 5 is 2,2-propylene or methylene, and S and T are each cyclohexylene or phenylene.
5. The uncured dental composite material of claim 4 wherein Q is selected from the group consisting of:
6. The uncured dental composite material of claim 1 wherein Q is selected from the group consisting of
7. The uncured dental composite material of claim 1 wherein R 2 ═R 3 and R 2 and R 3 are each a covalent bond or a methylene group.
8. The uncured dental composite material of claim 1 wherein the degree of polymerization is between 2 and 10.
9. The uncured dental composite material of claim 1 wherein a and a′ are both 5.
10. The uncured dental composite material of claim 9 , wherein R 2 and R 3 are each a methylene group, Q is 1,4-cyclohexylene, R 6 is a methyl group, and degree of polymerization is between 2 and 6.
11. The uncured dental composite material of claim 1 further comprising at least one photoinitiating accelerator, an activator, a pigment, a radiopaquing agent, a stabilizer, and an antioxidant.
12. A dental restoration article that is made by forming and curing the uncured dental composite material of claim 10 .
13. A composition comprising at least one compound of Formula I
E 1 -R 1 n —O—R 2 -Q-R 3 —O—R 4 m -E 2 I
wherein:
Q is selected from the group consisting of:
(ii) S—R 5 -T wherein S and T are each independently carbocyclic rings containing 5 or 6 carbon atoms with up to 3 C 1-3 alkyl substituents on the ring, and R 5 is a covalent bond or an alkylene group containing 1, 2, 3 or 4 carbon atoms; and
(iii) a carbocyclic fused ring system containing two fused rings containing a total of 8 to 10 carbon atoms with up to 4 C 1-3 alkyl substituents on the fused ring system;
R 2 and R 3 are each independently selected from the group consisting of a covalent bond and an alkylene group containing lto 4 carbon atoms;
R 1 is a repeat unit of the formula
R 4 is a repeat unit of the formula
E 1 and E 2 are each independently
wherein R 6 is H (acryloyl) or CH 3 (methacryloyl);
n and m are each independently an integer greater than 0;
a is independently an integer from 3 to 6;
a′ is independently an integer from 3 to 6; and
provided that neither R 2 nor R 3 is a covalent bond bonded directly to an aromatic ring; and
provided that the degree of polymerization of the compound is between 2 and 30.
14. The uncured dental composite material of claim 1 , wherein the total amount of the at least one filler is from about 50 weight percent to about 85 weight percent, based on the total weight of the uncured dental composite material.