Biaxially stretched polyester film
View Patent ↗The present invention relates to a biaxially stretched polyester film comprising a polyester layer A which comprises polybutylene terephthalate and at least one of a copolyester and an amorphous polyester, said biaxially stretched polyester film satisfying any one of the following requirements: (1) the polyester layer A exhibiting one melting point as measured by temperature-rise DSC method, and the polyester film having an edge tear resistance of not more than 100 N in each of longitudinal and width directions thereof; and (2) an average number of uncompatilized polybutylene terephthalate masses having a maximum length of not less than 1 μm which are present in a section of the layer A is not more than 1.0 per 100 μm 2 of the section of the layer A, and the polyester film having an edge tear resistance of not more than 100 N in each of longitudinal and width directions thereof.
1. A biaxially stretched polyester film comprising a polyester layer (layer A) which comprises polybutylene terephthalate homopolymer and at least one of a copolyester and an amorphous polyester, said biaxially stretched polyester film satisfying any one of the following requirements:
(1) the polyester layer (layer A) exhibiting one melting point as measured by temperature-ride DSC method, and the polyester film having an edge tear resistance of not more than 100 N in each of longitudinal and width directions thereof; and
(2) an average number of uncompatilized polybutylene terephthalate masses having a maximum length of not less than 1 μm which are present in a section of the layer A, being not more than 1.0 per 100 μm 2 of the section of the layer A, and the polyester film having an edge tear resistance of not more than 100 N in each of longitudinal and width directions thereof.
2. A biaxially stretched polyester film according to claim 1 , further comprising a polyester layer (layer B) having a melting point higher than the melting point of the layer A, the layer B being laminated on at least one surface of the layer A.
3. A biaxially stretched polyester film according to claim 2 , wherein the layer B has a thickness of not more than 8 μm.
4. A biaxially stretched polyester film according to claim 2 , wherein the layer B has a melting point higher 10°C. or more, than the melting point of the layer A.
5. A biaxially stretched polyester film according to claim 1 , wherein in the case of satisfying requirement (1) the polyester film has an edge tear resistance of 30 to 100 N in each of longitudinal directions thereof and in the case of satisfying requirement (2) the polyester film has an edge tear resistance of not more than 100 N and not less than 20 N in each of longitudinal and width directions thereof.