Direct synthesis of copper carbonate
View Patent ↗A basic copper salt selected from basic copper carbonate, basic copper sulfate, basic copper acetate, basic copper citrate, and basic copper nitrate is manufactured by contacting copper metal with an aqueous solution having ammonia; an acid selected from carbonic acid, sulfuric acid, acetic acid, nitric acid, or citric acid; and oxygen, under conditions where the copper metal is converted to the basic copper salt; and then recovering the basic copper salt. The most economical embodiment is where the ammonia is present in the aqueous solution is in an amount between about 6.7 g/l and about 15 g/l calculated as NH 3 , and the pH of the composition is between 8 and 10, and the temperature of the composition is between 25° C. and 100° C. The method is particularly useful if the basic copper salt is basic copper carbonate. The basic copper carbonate produced has the formula: (CuCO 3 ) x (Cu(OH 2 ) y , where y is 1 and x is between 0.1 to less than 1; or where y is 1 and x is 1, or where y is 1 and x is between 0.5 to less than about 0.95, or where y is 1 and x greater than 1.
1. A method of forming basic copper salt selected from basic copper carbonate, basic copper sulfate, basic copper acetate, and basic copper nitrate, the method comprising:
contacting copper metal with an aqueous solution comprising: an amine; an acid selected from carbonic acid, sulfuric acid, acetic acid, nitric acid, or citric acid; and oxygen, under conditions where the copper metal is converted to the basic copper salt; and
recovering the basic copper salt.
2. The method of claim 1 wherein the amine is ammonia.
3. The method of claim 2 wherein the amount of copper metal is such that there is at least one mole of copper for every two moles of ammonia.
4. The method of claim 3 wherein the amount of copper metal is such that there is at least 1.2 moles of copper metal for every mole of ammonia.
5. The method of claim 2 wherein the ammonia is present in the aqueous solution in an amount between about 6.7 g/l and about 15 g/l calculated as NH 3 .
6. The method of claim 5 wherein the ammonia is present in the aqueous solution in an amount between about 8 g/l and about 13 g/l calculated as NH 3 .
7. The method of claim 5 wherein the pH of the composition is between 8 and 10.
8. The method of claim 1 wherein the temperature of the composition is between 25° C. and boiling temperature.
9. The method of claim 1 wherein the basic copper salt is basic copper carbonate.
10. The method of claim 9 wherein the basic copper carbonate has the formula:
(CuCO 3 ) x ·(Cu(OH) 2 ) y , where y is 1 and x is between 0.1 to less than 1.
11. The method of claim 9 wherein the basic copper carbonate has the formula:
(CuCO 3 ) x ·(Cu(OH) 2 ) y , where y is 1 and x is between 0.5 to less than about 0.95.
12. The method of claim 9 wherein the basic copper carbonate has the formula:
(CuCO 3 ) x ·(Cu(OH) 2 ) y , where y is 1 and x greater than 1.
13. The method of claim 1 wherein the basic copper salt is basic copper sulfate.
14. The method of claim 13 wherein the basic copper sulfate has the formula:
(CuSO 4 ) x ·(Cu(OH) 2 ) y , where y is 3 and x is between 0.1 to less than 1.
15. The method of claim 13 wherein the basic copper sulfate has the formula:
(CuSO 4 ) x ·(Cu(OH) 2 ) y , where y is 3 and x is greater than 1.
16. The method of claim 1 wherein the basic copper salt is basic copper nitrate.
17. The method of claim 16 wherein the basic copper nitrate has the formula:
(Cu(NO 3 ) 2 ) x ·(Cu(OH) 2 ) y , where y is 3 and x is between 0.1 to less than 1.
18. The method of claim 16 wherein the basic copper nitrate has the formula:
(Cu(NO 3 ) 2 ) x ·(Cu(OH) 2 ) y , where y is 3 and x is greater than 1.
19. The method of claim 1 wherein the basic copper salt is basic copper acetate.
20. The method of claim 19 wherein the basic copper acetate has the formula:
(Cu(CH 3 COO) 2 ) x ·(Cu(OH) 2 ) y , where y is 1 and x is between 0.1 to less than 1.
21. The method of claim 5 wherein the process is a batch or a continuous process, and wherein the aqueous solution at the beginning of the reaction further comprises between 0.1 to 15 grams of soluble copper ions per liter of soluble copper.
22. A method of forming basic copper salt selected from basic copper carbonate, basic copper sulfate, basic copper acetate, and basic copper nitrate, the method comprising:
contacting copper (II) hydroxide with an aqueous solution comprising an amine and a sufficient amount of an acid selected from carbonic acid, sulfuric acid, acetic acid, nitric acid, or boric acid to convert at least one fourth of the copper hydroxide to the basic copper salt; under conditions where the copper hydroxide is converted to the basic copper salt; and
recovering the basic copper salt.
23. The method of claim 22 wherein the amine is ammonium hydroxide.
24. The method of claim 23 wherein the copper hydroxide is formed by contacting copper metal with an oxidant and an aqueous solution comprising ammonium hydroxide under conditions that the copper metal is converted to copper hydroxide.