Wood composites, methods of production, and methods of manufacture thereof
View Patent ↗An adhesive binder comprising a phenol-formaldehyde resin, polyvinyl ester resin, and a protein is disclosed. The adhesive binder is useful for preparing wood composites.
1. A wood composite comprising the cure product of an adhesive binder composition comprising a wood material and a thermosetting composition comprising,
a phenol-formaldehyde resin,
a polyvinyl ester resin, and
a protein;
provided, however, the wood composite does not contain any added urea-formaldehyde resin.
2. The wood composite of claim 1 wherein the protein is a vegetable protein.
3. The wood composite of claim 2 wherein the vegetable protein comprises a soy protein.
4. The wood composite of claim 3 wherein the soy protein is a soy flour.
5. The wood composite of claim 1 wherein the wood material is hardwood for plywood.
6. The wood composite of claim 1 wherein the wood material is selected from the group consisting of wood flakes, wood fibers, wood particles, wood wafers, wood strips, wood strands, wood veneer and combinations thereof.
7. The wood composite of claim 1 wherein the phenol-formaldehyde resin has a formaldehyde to phenol mole ratio of about 0.7:1 to about 4:1.
8. The wood composite of claim 1 wherein the ratio of the combined weights of the phenol-formaldehyde and polyvinyl ester resin solids to the protein is about 90:10 to about 50:50 in the thermosetting compound.
9. The wood composite of claim 1 wherein the polyvinyl ester resin is a polyvinyl acetate.
10. The wood composite of claim 1 wherein the adhesive binder further comprises additives selected from the group consisting of formaldehyde scavengers, plasticizers, thickeners, fillers, flame retardants, lubricants, softening agents, pigments, biocides, wax, acidic cure catalysts, and combinations thereof.
11. A process for making the wood composite of claim 1 comprising combining a wood material with an adhesive binder comprising a thermosetting composition comprising
a phenol-formaldehyde resin,
a polyvinyl ester resin, and
a protein;
consolidating the combined adhesive binder and wood material, and curing the combined adhesive binder and wood material.
12. The process of claim 11 wherein the protein is a vegetable protein.
13. The process of claim 12 wherein the vegetable protein comprises a soy protein.
14. The process of claim 13 wherein the soy protein is a soy flour.
15. The process of claim 11 wherein the wood material is selected from the group consisting of wood flakes, wood fibers, wood particles, wood wafers, wood strips, wood strands, wood veneer, and combinations thereof.
16. The process of claim 11 wherein the wood material is hardwood for plywood.
17. The process of claim 11 wherein the adhesive binder composition has a formaldehyde to phenol mole ratio of about 0.7:1 to about 4:1.
18. The process of claim 11 wherein the ratio of the combined weights of the phenol-formaldehyde and polyvinyl ester resin solids to the protein is about 90:10 to about 50:50 in the thermosetting compound.
19. The process of claim 11 wherein the adhesive binder further comprises additives selected from the group consisting of formaldehyde scavengers, plasticizers, thickeners, fillers, flame retardants, lubricants, softening agents, pigments, biocides, wax, acidic cure catalysts, and combinations thereof.
20. An adhesive binder, comprising a thermosetting composition comprising a
phenol-formaldehyde resin,
a polyvinyl ester resin, and
a protein;
provided, however, the adhesive binder contains no urea-formaldehyde resin.