Transparent member for electronic device
A transparent member for electronic device includes: polylactic acid, polymethyl(meth)acrylate, and a flame retardant, the transparent member having an Izod impact strength of 2.7-5 kJ/m 2 and a light transmittance at 400 nm-760 nm wavelength region of 40% or more. The transparent member for electronic device is made not from fossil resource, but mainly from a carbon-neutral material, and exhibits excellent flame retardancy, impact resistance and transparency.
1 . A transparent member for electronic device comprising:
polylactic acid,
polymethyl(meth)acrylate, and
a flame retardant,
the transparent member having an Izod impact strength of 2.7-5 kJ/m 2 and a light transmittance at 400 nm-760 nm wavelength region of 40% or more.
2 . The transparent member according to claim 1 , comprising
25-75 parts by weight of the polylactic acid,
30-75 parts by weight of polymethyl(meth)acrylate, and
0.1-30 parts by weight of the flame retardant.
3 . The transparent member according to claim 1 , wherein the polylactic acid consists essentially of
polylactic acid or
a blend of polylactic acid with a lactic acid copolymer of lactic acid and a monomer other than lactic acid.
4 . The transparent member according to claim 1 , wherein the flame retardant is at least one member selected from a phosphorus-containing flame retardant and a silicon-containing flame retardant.
5 . The transparent member according to claim 4 , wherein the phosphorus-containing flame retardant is at least one member selected from triphenyl phosphate, tricresyl phosphate and condensed phosphoric acid esters.
6 . The transparent member according to claim 4 , wherein the silicon-containing flame retardant is at least one member selected from silicone oil, modified silicone oil and silicone powder.
7 . The transparent member according to claim 1 , further comprising at least one member selected from a reinforcing agent, a nucleating agent and a plasticizer.
8 . The transparent member according to claim 7 , wherein the reinforcing agent is at least one member selected from natural fiber and regenerated fiber.
9 . The transparent member according to claim 7 , wherein the reinforcing agent is added in an amount of 10-30 parts by weight based on 100 parts by weight of the polylactic acid.
10 . The transparent member according to claim 7 , wherein the plasticizer is added in an amount of 0.1-1 part by weight based on 100 parts by weight of the polylactic acid.
11 . The transparent member according to claim 1 , wherein the member is obtained by directly feeding a mixture comprising the polylactic acid, the polymethyl(meth)acrylate and the flame retardant to a cylinder provided in an injection molding machine, melting and kneading the mixture, and conducting injection molding.
12 . The transparent member according to claim 11 , wherein the cylinder provided in the injection molding machine is equipped with a screw having kneading mechanism, and the member is obtained by mixing and kneading the mixture with the screw, and conducting injection molding.
13 . The transparent member according to claim 1 , which is used for an electrophotographic copier, a printer or a facsimile machine.
14 . The transparent member according to claim 1 , which is used as a copy receiving tray, a paper feed tray or a document tray.