Crystallizer temperature control via fluid control
View Patent ↗A method of crystallizing a plurality of crystallizable polymer pellets includes a step in which the pellets are contacted with a temperature adjusting fluid in a crystallizer. The fluid adjusts the temperature of the pellets by having a temperature sufficient to allow at least partial crystallization of the plurality of polymeric pellets while maintaining the average pellet temperature of the plurality of pellets below the melting temperature of the pellets. A crystallizer implementing the methods of the invention is also provided.
1. A method of crystallizing polymeric pellets in a crystallizer having an inlet, an outlet, and a contact region between the inlet and the outlet, the method comprising:
a) introducing a plurality of polymeric pellets, wherein the plurality of polymeric pellets have an initial average temperature between 135° C. and 200° C., into the inlet of the crystallizer, the plurality of polymeric pellets comprising a crystallizable polymer having a crystallization temperature and a melting temperature, the plurality of polymeric pellets having an average pellet temperature, wherein at least a portion of the plurality of pellets crystallize from inside to outside;
b) spraying a liquid into the contact region of the crystallizer, the liquid having a temperature sufficient to allow at least partial crystallization of the plurality of polymeric pellets while maintaining the average pellet temperature below the melting temperature while the plurality of polymeric pellets is within the crystallizer; and
c) removing the plurality of polymeric pellets from the outlet of the crystallizer wherein the crystallizer conveys the plurality of polymeric pellets along a longitudinal direction from the inlet to the outlet.
2. The method of claim 1 wherein the plurality of polymeric pellets introduced in step a) comprise regions having a temperature greater than or equal to the crystallization temperature of the polymer such that the plurality of polymeric pellets at least partially crystallize while inside the crystallizer.
3. The method of claim 1 wherein the liquid has a temperature sufficient to allow at least partial crystallization of the plurality of polymeric pellets while maintaining a maximum pellet temperature below the melting temperature while the plurality of polymeric pellets is within the crystallizer.
4. The method of claim 1 wherein the difference between the average pellet temperature in step a) and the crystallization temperature is less than the temperature rise induced by the crystallization of the plurality of polymeric pellets in the absence of cooling during step b).
5. The method of claim 1 wherein prior to the introducing step of step a), the plurality of polymeric pellets are formed by cutting polymeric strands using a strand cutter.
6. The method of claim 1 wherein the plurality of polymeric pellets are formed by cutting polymeric strands using a die face pellet cutter.
7. The method of claim 1 wherein the plurality of polymeric pellets after step c) have a degree of crystallinity equal to or greater than 30%.
8. The method of claim 1 wherein the plurality of polymeric pellets after step c) have a degree of crystallinity equal to or less than 70%.
9. The method of claim 1 wherein the plurality of polymeric pellets after step c) have a degree of crystallinity equal to or greater than 40%.
10. The method of claim 1 wherein a portion of the plurality of polymeric pellets are three dimensional objects characterized by a largest size dimension, the largest size dimension being less than 0.25 inches.
11. The method of claim 1 wherein a portion of the plurality of polymeric pellets have a spherical shape.
12. The method of claim 1 wherein a portion of the plurality of polymeric pellets have a cylindrical shape.
13. The method of claim 1 wherein a portion of the plurality of polymeric pellets have a rectangular cross section.
14. The method of claim 1 wherein the plurality of polymeric pellets comprise a component selected from the group consisting of polyester, polyolefins, polystyrenes, nylons, and polyketones.
15. The method of claim 1 wherein the plurality of polymeric pellets comprise polyethylene terephthalate.
16. The method of claim 1 wherein the plurality of polymeric pellets are introduced into the crystallizer in an amount of 5,000 lb/hr to 200,000 lb/hr.
17. The method of claim 1 wherein the liquid has a boiling point that is lower than a maximum temperature of the plurality of polymeric pellets.
18. The method of claim 17 further comprising the step of: d) separating the plurality of polymeric pellets from the liquid.
19. The method of claim 18 wherein step d) is performed prior to step c), after step c) or during step c).
20. The method of claim 18 wherein the plurality of polymeric pellets are separated from the liquid by centripetal force.
21. The method of claim 17 wherein the liquid is water.
22. The method claim 1 wherein the liquid has a boiling point that is higher than the average pellet temperature of the plurality of polymeric pellets.
23. The method of claim 1 wherein the plurality of polymeric pellets are agitated while being conveyed from the inlet to the outlet.
24. The method of claim 23 wherein the plurality of polymeric pellets are agitated by shaking.
25. The method of claim 24 wherein the plurality of polymeric pellets are agitated by directing the plurality of polymeric pellets to spiral.
26. The method of claim 1 wherein the crystallizer includes one or more sides that are at least partially insulated.
27. The method of claim 1 wherein the crystallizer includes one or more sides that are partially or completely uninsulated.
28. The method of claim 1 wherein the plurality of polymeric pellets are introduced into the crystallizer with a weight ratio of liquid to pellets from 1:2000 to 2000:1.
29. The method of claim 1 wherein the plurality of polymeric pellets have an average residence time from 1 second to 1 hour.
30. The method of claim 1 wherein the plurality of polymeric pellets have an average residence time from 1 minute to 10 minutes.
31. The method of claim 1 , further comprising, in a continuous process, melt phase polymerizing virgin polyester molten polymer, solidifying the molten polymer to form the plurality of polymeric pellets in contact with water, separating at least a portion of the water from the plurality of polymeric pellets, and introducing the plurality of polymeric pellets into a conveying system.
32. The method of claim 31 , wherein the plurality of polymeric pellets formed from solidifying the molten polymer have an It.V. of at least 0.70 d L/g.
33. The method of claim 32 , wherein the It.V. is at least 0.72 dL/g.
34. The method of claim 33 wherein the It.V. is at least 0.76 dL/g.
35. A crystallizer for crystallizing polymeric pellets, the crystallizer comprising:
an inlet for receiving a plurality of polymeric pellets;
a conveyor for transporting the plurality of polymeric pellets from a first location to a second location, the conveyor agitating the plurality of polymeric pellets as the plurality of polymeric pellets are being conveyed;
a liquid spray applicator for contacting the plurality of polymeric pellets with a liquid; and
an outlet for removing the plurality of polymeric pellets.
36. The crystallizer of claim 35 having an open top section.
37. The crystallizer of claim 36 wherein gas is transported across the surface of the pellets.
38. The crystallizer of claim 35 having a closed top section.
39. The crystallizer of claim 37 wherein the conveyor transports the plurality of polymeric pellets by agitation.
40. A method of crystallizing PET pellets in a crystallizer having an inlet, an outlet, and a contact region between the inlet and the outlet, the method comprising:
a) introducing a plurality of PET pellets into the inlet of the crystallizer, wherein the plurality of PET pellets have an initial average temperature between 135° C. and 200° C., the plurality of PET pellets being crystallizable polymer and having a crystallization temperature and a melting temperature, the plurality of PET pellets having an average pellet temperature;
b) spraying a liquid into the contact region of the crystallizer, the liquid having a temperature sufficient to allow at least partial crystallization of the plurality of PET pellets while maintaining the average pellet temperature below the melting temperature while the plurality of PET pellets is within the crystallizer wherein at least a portion of the plurality of PET pellets crystallize from inside to outside; and
c) removing the plurality of PET pellets from the outlet of the crystallizer wherein the crystallizer conveys the plurality of PET pellets along a longitudinal direction from the inlet to the outlet.