Diamond-silicon carbide composite and method
View Patent ↗Uniformly dense, diamond-silicon carbide composites having high hardness, high fracture toughness, and high thermal stability are prepared by consolidating a powder mixture of diamond and amorphous silicon. A composite made at 5 GPa/1673K had a measured fracture toughness of 12 MPa·m 1/2 . By contrast, liquid infiltration of silicon into diamond powder at 5 GPa/1673K produces a composite with higher hardness but lower fracture toughness.
1. A method for preparing an uniformly dense diamond-silicon carbide composite, comprising consolidating a powder mixture of diamond and amorphous silicon at a pressure and temperature sufficient to produce a uniformly dense diamond-silicon carbide composite having a Vickers hardness of at least 36 GPa, a Knoop hardness of at least 28 GPa, and a fracture toughness of at least 8 MPa·m 1/2 .