Surface conditioning prior to chemical conversion treatment of a steel member
View Patent ↗By subjecting a threaded joint for OCTG (oil country tubular goods) to surface conditioning with an aqueous solution of potassium tetraborate or sodium tetraborate prior to manganese phosphate chemical conversion treatment, a manganese phosphate chemical conversion coating having coarse crystal grains with an average crystal grain diameter of 10-110 micrometers is formed on the surface of the steel member which may be any steel including a high Cr steel. This manganese phosphate chemical conversion coating can hold a large amount of a liquid lubricant, and it is effective at preventing the occurrence of galling at the time of makeup of a threaded joint for OCTG.
1. A method of manufacturing a steel threaded joint for steel pipes characterized by:
treating a threaded joint with a surface conditioning solution, which is an aqueous solution containing an alkali metal tetraborate and not containing phosphate ions, and
directly after the surface conditioning treatment, carrying out a manganese phosphate chemical conversion treatment without washing between the surface conditioning treatment and the manganese phosphate chemical conversion treatment to form a conversion coating with coarse crystal grains having an average crystal grain diameter of 10-110 micrometers on the surface of the threaded joint.