Process for producing detachable dirt- and water-repellent surface coatings
View Patent ↗Process for producing detachable dirt- and water-repellent surface coatings on articles, wherein during the coating process, hydrophobic particles are applied to the surface of the articles, thus generating a surface structure with elevations on that surface of the articles that has dirt- and water-repellent properties, which comprises suspending the hydrophobic particles in a solution of a silicone wax in a highly volatile siloxane, and applying this suspension to at least one surface of an article, and then removing the highly volatile siloxane.
1. An impregnating composition for producing detachable surface coatings having dirt- and water repellant properties comprising a suspension including hydrophobic particles in a solution of a silicone wax in a highly volatile siloxane, wherein the silicone wax comprises at least one compound of general formula (II)
where
R is a hydrocarbon radical having from 10 to 20 carbon atoms,
n is from 2 to 85, and
m is from 2 to 60, the recrystallization points of said compounds of formula (II) is below about 20° C.
2. The composition as claimed in claim 1 wherein the highly volatile siloxane comprises at least one compound of general formula (I), a cyclic compound of general formula (Ia) or a mixture thereof
where
n is a number from 2 to 10.
3. The composition as claimed in claim 2 , wherein the highly volatile siloxane is a compound of formula (I) wherein n is from 2 to 5.
4. The composition as claimed in claim 2 , wherein the highly volatile siloxane is a compound of formula (Ia) wherein n is greater than or equal to 4 to less than or equal to 8.
5. The composition as claimed in claim 1 , wherein the hydrophobic particles have a fine structure in the nanometer range.
6. The composition as claimed in claim 1 , wherein the hydrophobic particles have an average particle diameter from 0.02 to 100 μm.
7. The composition as claimed in claim 1 , wherein the hydrophobic particles are selected from the group consisting of hydrophobicized silicas, zinc oxide, titanium dioxide and mixtures thereof.