Cold seal release films and methods of making same
View Patent ↗A cold seal release film including a cold seal release layer employing a silicone oil slip agent therein. The release layer is oxidatively treated to a level to reduce the cold seal release force by at least 25%, as compared to the cold seal release force without oxidative treatment of the release layer. A method of forming the cold seal release film with an improved cold seal release layer as described above also forms a part of the present invention.
1. A packaging film including a cold seal release film comprising a cold seal release layer for releasably engaging a cold seal adhesive, said packaging film having a cold seal receptive layer opposed to said cold seal release layer, said cold seal receptive layer retaining the cold seal adhesive thereon, said cold seal adhesive retained on said receptive layer being releasably engageable from said cold seal release layer; said cold seal release layer including a silicone oil slip agent therein and being oxidatively treated to reduce the release force of the release layer to the cold seal adhesive in engagement therewith relative to the release force of the release layer to the cold seal adhesive prior to said release layer being oxidatively treated.
2. The packaging film of claim 1 , said cold seal release layer comprising predominately one or more polyolefin polymers.
3. The packaging film of claim 1 , wherein said cold seal release layer has a matte finish having a 45 degree gloss less than 30.
4. The packaging film of claim 1 , wherein said cold seal release layer has a matte finish with a 45 degree gloss of 15 or less.
5. The packaging film of claim 1 , wherein said cold seal release layer has a matte finish with a 45 degree gloss of 10 or less.
6. The packaging film of claim 3 , wherein said cold seal release layer has a static coefficient of friction of less than 0.5 and a kinetic coefficient of friction of less than 0.4.
7. The packaging film of claim 3 , wherein said cold seal release layer has a static coefficient of friction less than 0.35 and a kinetic coefficient of friction of less than 0.25.
8. The packaging film of claim 1 , wherein said oxidative treatment is corona treatment.
9. The packaging film of claim 1 , wherein said silicone oil is polydimethylsiloxane.
10. The packaging film of claim 9 , wherein said polydimethylsiloxane is present in an amount of at least 0.0 5% by weight of the cold seal release layer.
11. The packaging film of claim 1 being in a roll with the cold seal adhesive retained on the cold seal adhesive receptive layer releasably engaging the cold seal release layer.
12. The packaging film of claim 1 wherein the cold seal adhesive receptive layer to which the cold seal adhesive is retained is a layer of the cold seal release film opposed to said cold seal release layer.
13. The packaging film of claim 1 including a second film adhered to the cold seal release film, said cold seal adhesive receptive layer opposed to said cold seal release layer being an exposed surface of said second film.
14. A method of making a packaging film including a cold seal release layer thereon for releasably engaging a cold seal adhesive, said method including the following steps:
a. forming a cold seal release film with said cold seal release layer on one surface, said cold seal release layer including a polymer composition having cold seal release properties and including in that polymer composition a silicone oil slip agent;
b. oxidatively treating said cold seal release layer at a level to reduce the cold seal release force to said cold seal adhesive at least 25% of the cold seal release force before oxidative treatment;
c. applying the cold seal adhesive to a cold seal adhesive receptive layer opposed to said cold seal release layer for retaining said cold seal adhesive on said receptive layer; and
d. bringing said cold seal adhesive retained on the receptive layer into releasable engagement with the cold seal release layer.
15. The method of claim 14 including forming the cold seal release layer from predominantly one or more polyolefin polymers.
16. The method of claim 14 including employing a polymer composition for the release layer that provides a matte finish having a 45 degree gloss less than 30.
17. The method of claim 14 including employing a polymer composition for the release layer that provides a matte finish having a 45 degree gloss of 15 or less.
18. The method of claim 14 including employing a polymer composition for the release layer that provides a matte finish having a 45 degree gloss of 10 or less.
19. The method of claim 14 wherein said oxidative treatment is corona treatment.
20. The method of claim 14 wherein the silicone oil slip agent is added in an amount of at least 0.05% by weight of the cold seal release layer.
21. The method according to claim 14 wherein the silicone oil slip agent is added in an amount of at least 0.1% by weight of the layer.
22. The method of claim 14 wherein the silicone oil slip agent that is added is polydimethylsiloxane.
23. The method of claim 14 , wherein the cold seal adhesive receptive layer is a layer of the cold seal release film opposed to the cold seal release layer, said step of forming the packaging film includes applying the cold seal adhesive to the receptive layer of the cold seal release film.
24. The method of claim 14 including the additional step of laminating the cold seal release film to a second film, said cold seal adhesive receptive layer being a layer of said second film.
25. The method of claim 24 wherein the cold seal release film is a clear film.