US 8,003,042 · App. 11/469,407 · Granted Aug 23, 2011

Toughened silicon carbide and method for making the same

View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 8,003,042
App. No.
11/469,407
Granted
Aug 23, 2011
Kind
B2
Abstract

Pressureless sintering of silicon carbide with fracture toughness in excess of about 4 MPa-m 1/2 as measured by the single-edge precracked beam (SEPB) technique while maintaining a density greater than 3.1 g/cc for compositions with SiC greater than about 94 wt. % is made possible through the use of metallic Al to promote sintering and grain growth. Boron and carbon may be used as traditional sintering aids, with nitrogen to suppress grain growth, and additions of yttrium and/or lanthanide elements to promote intergranular fracture.

Claims (64)

1. A method of forming a sintered ceramic body comprising predominantly by weight silicon carbide, the method comprising the steps of:

a) forming a green body from a mixture comprising the components:

SiC;

aluminum in elemental form;

a rare earth metal in elemental or combined form;

boron in elemental or combined form; and

nitrogen; and

b) heating the green body under conditions resulting in a sintered ceramic body comprising at least 94 wt. % SiC, having a density above about 3.1 g/cc, and exhibiting an intergranular fracture mechanism.

2. The method of claim 1 , wherein the heating step comprises pressureless sintering.

3. The method of claim 1 , wherein the heating step comprises cladless hot isostatic pressing.

4. The method of claim 1 , wherein the amount of SiC in the mixture is 94 weight % or more.

5. The method of claim 1 , wherein the amount of rare earth metal comprises less than about 2.5% by weight of the mixture.

6. The method of claim 5 , wherein the amount of rare earth metal comprises less than about 1.5% by weight of the mixture.

7. The method of claim 6 , wherein the amount of rare earth metal comprises less than about 1% by weight of the mixture.

8. The method of claim 7 , wherein the amount of rare earth metal comprises greater than about 0.01% by weight of the mixture.

9. The method of claim 8 , wherein the amount of rare earth metal comprises greater than about 0.05% by weight of the mixture.

10. The method of claim 9 , wherein the amount of rare earth metal comprises greater than about 0.1% by weight of the mixture.

11. The method of claim 1 , wherein the amount of aluminum comprises less than about 5% by weight of the mixture.

12. The method of claim 11 , wherein the amount of aluminum comprises less than about 3% by weight of the mixture.

13. The method of claim 12 , wherein the amount of aluminum comprises less than about 1% by weight of the mixture.

14. The method of claim 13 , wherein the amount of aluminum comprises greater than about 0.25% by weight of the mixture.

15. The method of claim 1 , wherein the amount of aluminum present in elemental form comprises greater than about 50% by weight of the aluminum present.

16. The method of claim 1 , wherein the boron is present at least in part as boron carbide.

17. The method of claim 1 , wherein the amount of boron comprises less than about 1% by weight of the mixture.

18. The method of claim 17 , wherein the amount of boron comprises less than 0.5% by weight of the mixture.

19. The method of claim 18 , wherein the amount of boron comprises greater than 0.1% by weight of the mixture.

20. The method of claim 1 , wherein the mixture further comprises carbon in elemental or combined form.

21. The method of claim 20 , wherein the carbon in elemental or combined form comprises a source of carbon that generates carbon during the heating step.

22. The method of claim 21 , wherein the source of carbon is a resin.

23. The method of claim 21 , wherein the source of carbon is present in an amount that results in a carbon content of less than about 1% by weight in the sintered ceramic body.

24. The method of claim 1 , wherein the nitrogen in combined form is selected from the group consisting of AlN, Si 3 N 4 , BN, and combinations thereof.

25. The method of claim 1 , wherein the amount of nitrogen comprises less than about 2% by weight of the mixture.

26. The method of claim 25 , wherein the amount of nitrogen comprises less than about 1% by weight of the mixture.

27. The method of claim 26 , wherein the amount of nitrogen comprises greater than about 0.1% by weight of the mixture.

28. The method of claim 1 , wherein the silicon carbide comprises particles having a surface area greater than about 10 m 2 ·g −1 .

29. The method of claim 1 , wherein the heating step comprises pressureless sintering said mixture without powder beds, and without gas pressures above 0.2 MPa, at a temperature between 1800° C. and 2200° C. for a time between 15 minutes and 240 minutes.

30. The method of claim 1 , wherein the heating step results in a sintered body having a fracture toughness greater than about 4 MPa·m 1/2 as measured by the single-edged precracked beam technique.

31. The method of claim 1 , wherein the sintered ceramic body has a fracture toughness greater than about 6 MPa·m 1/2 as measured by the single-edged precracked beam technique.

32. A sintered ceramic body obtained from the process of claim 1 .

33. The method of claim 1 , wherein the rare earth is present as an oxide with all other components having only surface oxides present due to adsorption.

34. A method of forming a sintered ceramic body comprising predominantly by weight silicon carbide, the method comprising the steps of:

a) forming a green body from a mixture comprising:

SiC comprising at least 94 weight percent of the mixture;

aluminum in elemental form and comprising between about 0.25 and about 5 percent by weight of the mixture;

rare earth metal in elemental or combined form comprising between about 0.01 and about 2.5 percent by weight of the mixture;

boron in elemental or combined form comprising between about 0.1 and about 2.5 percent by weight of the mixture;

carbon such that after application of a heating step the carbon is less than about 1% by weight in the sintered ceramic body; and

nitrogen in combined form comprising between about 0.1 and about 2 percent by weight; and

b) heating the green body under conditions resulting in a sintered ceramic body exhibiting an intergranular fracture mechanism.

35. The sintered ceramic body made by the process of claim 34 , wherein the density is greater than about 3.0 g/cc.

36. The sintered ceramic body made by the process of claim 34 , wherein the density is greater than about 3.1 g/cc.

37. A sintered ceramic body, comprising:

at least 94 weight percent silicon carbide;

between about 0.25 and about 3 weight percent aluminum;

between about 0.01 and about 1.0 weight percent of material selected from the group consisting of periodic table elements Y, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, and combinations thereof;

between about 0.1 and about 0.5 weight percent boron;

between about 0.15 and about 1 weight percent nitrogen;

having a density above 3.1 g/cc; and

having a fracture toughness greater than about 4 MPa·m 1/2 as measured by the single-edged precracked beam technique.

38. The sintered ceramic body of claim 37 , further comprising between about 0.1 to about 1.5 weight percent carbon.

39. The sintered ceramic body of claim 37 , further comprising less than about 0.4 weight percent of material from the group consisting of periodic table elements Y, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, and combinations thereof.

40. The sintered ceramic body of claim 37 , wherein the SEPB fracture toughness is greater than about 5 MPa-m 1/2 as measured by the single-edged precracked beam technique.

41. The sintered ceramic body of claim 37 , wherein the SEPB fracture toughness is greater than about 6 MPa-m 1/2 as measured by the single-edged precracked beam technique.

42. The sintered ceramic body of claim 37 , wherein the density is greater than about 3.15 g/cc.

Assignments (5)
TERMINATION AND RELEASE OF CONFIRMATORY GRANT OF SECURITY INTEREST IN PATENTS Recorded Oct 29, 2025
From: JPMORGAN CHASE BANK, N.A.
To: COORSTEK, INC.
Reel/Frame 073424/0583 →
SECURITY INTEREST Recorded Oct 28, 2025
From: COORSTEK, INC.
To: CITIBANK, N.A., AS COLLATERAL AGENT
Reel/Frame 072705/0315 →
SECURITY INTEREST Recorded May 29, 2025
From: COORSTEK, INC.
To: JPMORGAN CHASE BANK, N.A.
Reel/Frame 071248/0824 →
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Feb 27, 2023
From: CERAMATEC, INC
To: COORSTEK, INC.
Reel/Frame 062876/0001 →
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Jun 22, 2007
From: CUTLER, RAYMOND; FLINDERS, MARC; RAY, DARIN
To: CERAMATEC, INC.
Reel/Frame 019470/0381 →