Superabsorbent polymer with high permeability
View Patent ↗The invention relates to absorptive, crosslinked polymers which are based on partly neutralized, monoethylenically unsaturated monomers carrying acid groups wherein the absorptive crosslinked polymer may be coated with a thermoplastic polymer, and have improved properties, in particular in respect of their capacity for transportation of liquids in the swollen state, and which has a high gel bed permeability and high centrifuge retention capacity.
1. A sanitary article comprising a superabsorbent polymer composition comprising a superabsorbent polymer consisting essentially of:
a) from about 55 to about 99.9 wt.% of polymerizable unsaturated acid group containing monomers;
b) from about 0.001 to about 5.0% by weight of internal crosslinking agent based on the weight of a);
wherein elements a) and b) are polymerized and prepared into superabsorbent polymer particles; wherein the superabsorbent polymer particles further comprise the following surface additives
c) from about 0.001 to about 5.0% by weight of surface crosslinking agent applied to the particle surface based on dry polymer powder weight;
d) from about 0.01% to about 5 wt.% by weight of a penetration modifier immediately before, during or immediately after the surface crosslinking agent based on dry polymer powder weight;
e) from 0 to about 5% by weight of a multivalent metal salt on the particle surface based on dry polymer powder weight;
f) from 0 to about 2% by weight of a surfactant on the particle surface based on dry polymer powder weight;
g) from about 0.01 to about 5% by weight of an insoluble, inorganic powder based on dry polymer powder weight; and
h) from about 0.01 to about 0.5% by weight of a thermoplastic polymer based on dry polymer powder weight, said thermoplastic polymer having a thermoplastic melt temperature wherein the thermoplastic polymer is applied on and fully encapsulates the particle surface coincident with or followed by a temperature at least about the thermoplastic melt temperature or greater,
wherein the superabsorbent polymer composition has a degree of neutralization of more than about 25%; and having the characteristics of centrifuge retention capacity of about 25 g/g or more; a gel bed permeability I of about 500 ×10 −9 cm 2 or more; or a gel bed permeability II of about 300 ×10 −9 cm 2 or more.
2. The sanitary article according to claim 1 wherein the superabsorbent polymer composition has a gel bed permeability I of at least about [54000e −0.18× +100]×10 −9 cm 2 wherein x is the numeric value of the centrifuge retention capacity.
3. The sanitary article according to claim 1 wherein the superabsorbent polymer composition has a gel bed permeability I of at least about [54000e −0.165x +100]×10 −9 cm 2 wherein x is the numeric value of the centrifuge retention capacity.
4. The sanitary article of claim 1 wherein the thermoplastic polymer is selected from polyethylene, polyesters, polyurethanes, linear low density polyethylene (LLDPE), ethylene acrylic acid copolymer (EAA), styrene copolymers, ethylene alkyl methacrylate copolymer (EMA), polypropylene (PP), ethylene vinyl acetate copolymer (EVA) or blends thereof, or copolymers thereof.
5. The sanitary article of claim 1 wherein the superabsorbent polymer composition has a Dust Value of about 4 or less.
6. The sanitary article of claim 1 wherein the superabsorbent polymer composition has a gel bed permeability I of about 800 ×10 −9 cm 2 or more; or a gel bed permeability II of about 500 ×10 −9 cm 2 or more.
7. The sanitary article of claim 1 wherein the superabsorbent polymer composition has a shear modulus of less than about 9500 dynes/cm 2 .
8. The sanitary article of claim 1 wherein the sanitary article is a diaper.
9. A sanitary article comprising a superabsorbent polymer consisting essentially of:
a) from about 55 to about 99.9 wt.% of polymerizable unsaturated acid group containing monomers;
b) from about 0.001 to about 5.0 wt.% based on the weight of a) of internal crosslinking agent;
wherein elements a) and b) are polymerized and prepared into superabsorbent polymer particles; wherein the superabsorbent polymer particles further comprise the following surface additives
c) from about 0.001 to about 5.0% by weight of surface crosslinking agent applied to the particle surface based on dry polymer powder weight;
d) from about 0.01% to about 5% by weight of a penetration modifier immediately before, during or immediately after the surface crosslinking agent based on dry polymer powder weight;
e) from 0 to about 5% by weight of a multivalent metal salt on the particle surface based on dry polymer powder weight;
f) from 0 to about 2% by weight of a surfactant on the particle surface based on dry polymer powder weight;
g) from about 0.01 to about 5% by weight of an insoluble, inorganic powder based on dry polymer powder weight; and
h) from about 0.01 to about 0.5% by weight of a thermoplastic polymer based on dry polymer powder weight, the thermoplastic polymer having a thermoplastic melt temperature wherein the thermoplastic polymer is applied on and fully encapsulates the particle surface coincident with or followed by a temperature at least about the thermoplastic melt temperature or greater,
wherein the composition has a degree of neutralization of more than about 25%; having the characteristics of centrifuge retention capacity of about 25 g/g or more; a gel bed permeability I of about 200 ×10 −9 cm 2 or more; or a gel bed permeability II of about 150 ×10 −9 cm 2 or more.
10. The sanitary article according to claim 9 wherein the superabsorbent polymer composition has a gel bed permeability I of at least about [54000e −0.18x +100]×10 −9 cm 2 wherein x is the numeric value of the centrifuge retention capacity.
11. The sanitary article according to claim 9 wherein the superabsorbent polymer composition has a gel bed permeability I of at least about [54000e −0.18x +100] ×10 −9 cm 2 wherein x is the numeric value of the centrifuge retention capacity.
12. The sanitary article of claim 9 wherein the thermoplastic polymer is selected from polyethylene, polyesters, polyurethanes, linear low density polyethylene (LLDPE), ethylene acrylic acid copolymer (EAA), styrene copolymers, ethylene alkyl methacrylate copolymer (EMA), polypropylene (PP), ethylene vinyl acetate copolymer (EVA) or blends thereof, or copolymers thereof.
13. The sanitary article of claim 9 wherein the superabsorbent polymer composition has a Dust Value of about 4 or less.
14. The sanitary article of claim 9 wherein the superabsorbent polymer composition has a shear modulus of less than about 9500 dynes/cm 2 .
15. The sanitary article of claim 9 wherein the superabsorbent polymer composition has a shear modulus from about 4000 dynes/cm 2 to about 8500 dynes/cm 2 .
16. The sanitary article according to claim 1 wherein the superabsorbent polymer composition comprises from about 0.1 to about 5% by weight of a multivalent metal salt based on the dry polymer powder weight.
17. The sanitary article of claim 1 wherein the insoluble, inorganic powder is silica.
18. The sanitary article of claim 9 wherein the insoluble, inorganic powder is silica.
19. The sanitary article of claim 1 wherein the superabsorbent polymer composition has from about 0.01 to about 0.1% by weight of a thermoplastic polymer based on dry polymer powder weight.
20. The sanitary article of claim 9 wherein the superabsorbent polymer composition has from about 0.01 to about 0.1% by weight of a thermoplastic polymer based on dry polymer powder weight.
21. A superabsorbent polymer composition comprising a superabsorbent polymer consisting essentially of:
a) from about 55 to about 99.9 wt.% of polymerizable unsaturated acid group containing monomers;
b) from about 0.001 to about 5.0% by weight of internal crosslinking agent based on the weight of a);
wherein elements a) and b) are polymerized and prepared into superabsorbent polymer particles; wherein the superabsorbent polymer particles further comprise the following surface additives
c) from about 0.001 to about 5.0% by weight of surface crosslinking agent applied to the particle surface based on dry polymer powder weight;
d) from about 0.01% to about 5 wt.% by weight of a penetration modifier immediately before, during or immediately after the surface crosslinking agent based on dry polymer powder weight;
e) from 0 to about 5% by weight of a multivalent metal salt on the particle surface based on dry polymer powder weight wherein the multivalent metal salt includes an aluminum cation;
f) from 0 to about 2% by weight of a surfactant on the particle surface based on dry polymer powder weight;
g) from about 0.01 to about 5% by weight of an insoluble, aluminum inorganic powder based on dry polymer powder weight; and
h) from about 0.01 to about 0.5% by weight of a thermoplastic polymer based on dry polymer powder weight, said thermoplastic polymer having a thermoplastic melt temperature wherein the thermoplastic polymer is applied on and fully encapsulates the particle surface coincident with or followed by a temperature at least about the thermoplastic melt temperature or greater,
wherein the superabsorbent polymer composition has a degree of neutralization of more than about 25%; and having the characteristics of centrifuge retention capacity of about 25 g/g or more; a gel bed permeability I of about 500 ×10 −9 cm 2 or more; or a gel bed permeability II of about 300 ×10 −9 cm 2 or more.
22. The superabsorbent polymer composition of claim 21 wherein the thermoplastic polymer comprises polypropylene.
23. The sanitary article according to claim 1 wherein the superabsorbent polymer composition has a degree of neutralization of more than about 25%; and having the characteristics of centrifuge retention capacity of about 25 g/g or more; a gel bed permeability I of about 500 ×10 −9 cm 2 or more; or a gel bed permeability II of about 300 ×10 −9 cm 2 or more.
24. The sanitary article according to claim 1 wherein the superabsorbent polymer composition has a gel bed permeability I of at least about [54000e −0.165x +100] x10 −9 cm 2 wherein x is the numeric value of the centrifuge retention capacity.
25. The sanitary article of claim 1 wherein the thermoplastic polymer is selected from polyethylene, polyesters, polyurethanes, linear low density polyethylene (LLDPE), ethylene acrylic acid copolymer (EAA), styrene copolymers, ethylene alkyl methacrylate copolymer (EMA), polypropylene (PP), ethylene vinyl acetate copolymer (EVA) or blends thereof, or copolymers thereof.
26. The sanitary article of claim 1 wherein the superabsorbent polymer composition has a Dust Value of about 4 or less.
27. The sanitary article of claim 1 wherein the superabsorbent polymer composition has a shear modulus of less than about 9500 dynes/cm 2 .
28. The sanitary article of claim 1 wherein the sanitary article is a diaper.