Entrapping immobilization pellets and process for producing the same
The present invention produces entrapping immobilization pellets which have high pellet strength and retain high and stable microbial activity (nitrification activity) even if a low concentration of a material involved in immobilization (such as an immobilizing material or polymerization initiator) used. The entrapping immobilization pellets in which microorganisms are entrapped and immobilized in an immobilizing material comprise a filler having a plate-like and/or needle-like crystal structure in the immobilizing material.
1 . Entrapping immobilization pellets in which microorganisms are entrapped and immobilized in an immobilizing material, the entrapping immobilization pellets comprising:
a filler having a plate-like and/or needle-like crystal structure in the immobilizing material.
2 . The entrapping immobilization pellets according to claim 1 , wherein the plate-like and/or needle-like filler is an inorganic filler.
3 . The entrapping immobilization pellets according to claim 1 , wherein the plate-like and/or needle-like filler has an average particle size of 12 μm or less.
4 . The entrapping immobilization pellets according to claim 2 , wherein the plate-like and/or needle-like filler has an average particle size of 12 μm or less.
5 . The entrapping immobilization pellets according to claim 1 , wherein the mass ratio F/P of the mass of the plate-like and/or needle-like filler F to the mass of the immobilizing material P is 0.01 to 5.
6 . The entrapping immobilization pellets according to claim 2 , wherein the mass ratio F/P of the mass of the plate-like and/or needle-like filler F to the mass of the immobilizing material P is 0.01 to 5.
7 . The entrapping immobilization pellets according to claim 3 , wherein the mass ratio F/P of the mass of the plate-like and/or needle-like filler F to the mass of the immobilizing material P is 0.01 to 5.
8 . The entrapping immobilization pellets according to claim 4 , wherein the mass ratio F/P of the mass of the plate-like and/or needle-like filler F to the mass of the immobilizing material P is 0.01 to 5.
9 . The entrapping immobilization pellets according to claim 1 , wherein the concentration of the plate-like and/or needle-like filler is 0.1 to 20 mass % based on the entrapping immobilization pellets, and the concentration of the immobilizing material is 2 to 15 mass % based on the entrapping immobilization pellets.
10 . The entrapping immobilization pellets according to claim 2 , wherein the concentration of the plate-like and/or needle-like filler is 0.1 to 20 mass % based on the entrapping immobilization pellets, and the concentration of the immobilizing material is 2 to 15 mass % based on the entrapping immobilization pellets.
11 . The entrapping immobilization pellets according to claim 3 , wherein the concentration of the plate-like and/or needle-like filler is 0.1 to 20 mass % based on the entrapping immobilization pellets, and the concentration of the immobilizing material is 2 to 15 mass % based on the entrapping immobilization pellets.
12 . The entrapping immobilization pellets according to claim 4 , wherein the concentration of the plate-like and/or needle-like filler is 0.1 to 20 mass % based on the entrapping immobilization pellets, and the concentration of the immobilizing material is 2 to 15 mass % based on the entrapping immobilization pellets.
13 . The entrapping immobilization pellets according to claim 5 , wherein the concentration of the plate-like and/or needle-like filler is 0.1 to 20 mass % based on the entrapping immobilization pellets, and the concentration of the immobilizing material is 2 to 15 mass % based on the entrapping immobilization pellets.
14 . The entrapping immobilization pellets according to claim 6 , wherein the concentration of the plate-like and/or needle-like filler is 0.1 to 20 mass % based on the entrapping immobilization pellets, and the concentration of the immobilizing material is 2 to 15 mass % based on the entrapping immobilization pellets.
15 . The entrapping immobilization pellets according to claim 7 , wherein the concentration of the plate-like and/or needle-like filler is 0.1 to 20 mass % based on the entrapping immobilization pellets, and the concentration of the immobilizing material is 2 to 15 mass % based on the entrapping immobilization pellets.
16 . The entrapping immobilization pellets according to claim 8 , wherein the concentration of the plate-like and/or needle-like filler is 0.1 to 20 mass % based on the entrapping immobilization pellets, and the concentration of the immobilizing material is 2 to 15 mass % based on the entrapping immobilization pellets.
17 . A process for producing entrapping immobilization pellets in which microorganisms are entrapped and immobilized in an immobilizing material, the process comprising:
mixing the immobilizing material with a filler having a plate-like and/or needle-like crystal structure, and then mixing the mixture with the microorganisms to form a gel.
18 . The process for producing entrapping immobilization pellets according to claim 17 , wherein the plate-like and/or needle-like filler is an inorganic filler.