Cell with copper oxide cathode
View Patent ↗An electrochemical battery cell with Cu x O, where x is from 0.9 to 1.3, as a positive electrode active material. The specific surface area of the Cu x O is from 1.0 to 4.0 m 2 /gram, preferably from 1.0 to 2.9 m 2 /g to provide an increase in the high voltage discharge capacity of the Cu x O.
1. An electrochemical battery cell comprising:
a cell container;
a positive electrode comprising a positive electrode active material;
a negative electrode comprising a negative electrode active material comprising zinc;
a separator disposed between the positive and negative electrodes; and
an electrolyte;
wherein the positive electrode active material comprises copper oxide and one or more additional active materials, the one or more additional positive electrode active materials comprises manganese dioxide, the copper oxide has a formula Cu x O, where x is from 0.9 to 1.3, and the copper oxide has a BET specific surface area from 1.0 to 2.9 m 2 /gram.
2. The cell defined in claim 1 , wherein the Cu x O comprises particles that have a D 50 value less than 50 μm and a D 10 value from 1.0 to 3.0 μm, as measured by laser diffraction analysis using a unified scatter technique.
3. The cell defined in claim 1 wherein the electrolyte comprises an aqueous alkaline solution.
4. An electrochemical battery cell comprising:
a cell container;
a positive electrode comprising a positive electrode active material;
a negative electrode comprising a negative electrode active material comprising zinc;
a separator disposed between the positive and negative electrodes; and
an aqueous alkaline electrolyte; wherein
the positive electrode active material comprises copper oxide having a formula Cu x O, where x is from 0.9 to 1.3, a BET specific surface area from 1.0 to 2.9 m 2 /gram, and a particle size distribution with a D 50 value less than 50 μm as measured by laser diffraction analysis using a unified scatter technique, and the positive electrode active material further comprises manganese dioxide.
5. The cell defined in claim 4 , wherein the BET specific surface area is from 1.45 to 2.9 m 2 /gram.
6. The cell defined in claim 5 , wherein the BET specific surface area is from 1.7 to 2.9 m 2 /gram.
7. The cell defined in claim 4 , wherein the particle size distribution further has a D 10 value from 1.0 to 2.0 μm.
8. The cell defined in claim 7 , wherein the D 10 value is from 1.0 to 1.7 μm.
9. The cell defined in claim 4 , wherein the Cu x O has an average primary particle size from 0.3 to 5.0 μm.
10. The cell defined in claim 9 , wherein the average primary particle size is from 0.3 to 1.0 μm.
11. The cell defined in claim 1 , wherein the positive electrode further comprises graphite, and the graphite consists essentially of a non-expanded graphite powder.
12. The cell defined in claim 4 , wherein the positive electrode further comprises graphite, and the graphite consists essentially of a non-expanded graphite powder.