Transparent articles with anti-reflective coating and methods of making the same
View Patent ↗Anti-reflective (AR) coated transparent substrates and methods of making the same are provided wherein the AR coating includes a fluorinated polymer. Preferably, the anti-reflective transparent articles and methods of making the same include a transparent substrate (e.g., glass), and an anti-reflective coating formed of a fluorinated polymer on one (or both) surface(s) of the substrate. If coated on both surfaces of the glass sheet, the fluorinated polymer forming one of the coatings may be the same or different as compared to the fluorinated polymer forming the other coating. In especially preferred embodiments, the fluorinated polymer is the reaction product of at least one fluorinated acrylic ester monomer which is formed over an anchor layer of a hydrolyzed unsaturated alkyl silane adsorbed onto the substrate surface.
1. A method of making an anti-reflective transparent article comprising the steps of:
(a) applying onto at least one surface of a transparent substrate an aqueous solution consisting essentially of a hydrolyzed unsaturated alkyl silane and allowing the aqueous solution to be in contact with the at least one surface of the transparent substrate for a time sufficient to allow the hydrolyzed unsaturated alkyl silane to be adsorbed into the at least one surface thereof and form an anchor layer thereon;
(b) applying a liquid reaction mixture onto a surface of the anchor layer, wherein the liquid reaction mixture is comprised of at least one fluorinated alkyl ester monomer in the presence of an acrylic acid, an ethyleneglycol diacrylate cross-linker and a photoinitiator; and
(c) photopolymerizing the liquid reaction mixture to form a polymeric anti-reflective coating on the anchor layer.
2. The method of claim 1 , wherein the substrate is a glass sheet having opposed surfaces, and wherein steps (a)-(c) are practiced by applying a coating onto both of the opposed surfaces of the glass sheet.
3. The method of claim 1 , wherein steps (a)-(c) are practiced to achieve a coating thickness of between about 50 nm to about 200 nm.
4. The method of claim 1 , wherein the at least one fluorinated alkyl ester monomer is selected from the group consisting of:
CH2=C(H)COOCH2CF3
CH2=C(CH3)COOCH2CF3
CH2=C(H)COOCH2CF2CF2H
CH2=C(CH3)COOCH2CF2CF2H
CH2=C(H)COOCH(CF3)2
CH2=C(CH3)COOCH(CF3)2
CH2=C(H)COOCH2(CF2)3F
CH2=C(CH3)COOCH2(CF2)3F
CH2=C(H)COOCH2(CF2)4H
CH2=C(CH3)COOCH2(CF2)4H
CH2=C(H)COOCH2(CF2)F
CH2=C(CH3)COOCH2(CF2)F
CH2=C(H)COO(CH2)2(CF2)8F
CH2=C(CH3)COO(CH2)2(CF2)8F
CH2=C(H)COOCH2CF(CF3)OCF2(CF3)O(CF2)4F
CH2=C(CH3)COOCH2CF(CF3)OCF2(CF3)O(CF2)4F
(CF3)2(CO2CF═CF).
5. An anti-reflective transparent article comprising:
a transparent substrate,
an anchor layer adsorbed onto at least one surface of the transparent substrate, and
an anti-reflective coating applied onto a surface of the anchor layer, wherein
the anchor layer consists essentially of an unsaturated alkyl silane, and wherein
the anti-reflective coating is a photopolymerized reaction product comprised of at least one fluorinated alkyl ester monomer in the presence of an acrylic acid, an ethyleneglycol diacrylate cross-linker and a photoinitiator.
6. An article as in claim 5 , wherein the liquid reaction mixture comprises at least about 85 parts by weight of the at least one fluorinated alkyl ester monomer, about 5 parts by weight or less of the acrylic acid, between about 0.25 to 2.5 parts by weight of the ethyleneglycol diacrylate cross— linker, and between about 0.1 to about 1.0 parts by weight of the photoinitiator, based on 100 parts by weight of the liquid reaction mixture.
7. An article as in claim 6 , wherein the liquid reaction mixture comprises about 96 parts by with of the fluorinated alkyl monomer, about 2 parts by weight of acrylic acid, about 1 part of ethyleneglycol dimethacrylate, and about 0.5 part of p-xylenebis(N,N-diethyldithiocarbamate).
8. An article as in claim 5 , wherein the transparent substrate is a glass sheet having an anti-reflective coating comprised of the photopolymerized reaction product, which may be the same or different, on the opposed surfaces thereof.
9. An article as in claim 5 , wherein the anti-reflective coating has a thickness of between about 50 nm to about 200 nm.
10. An article as in claim 5 , wherein the at least one fluorinated alkyl ester monomer is selected from the group consisting of:
CH2=C(H)COOCH2CF3
CH2=C(CH3)COOCH2CF3
CH2=C(H)COOCH2CF2CF2H
CH2=C(CH3)COOCH2CF2CF2H
CH2=C(H)COOCH(CF3)2
CH2=C(CH3)COOCH(CF3)2
CH2=C(H)COOCH2(CF2)3F
CH2=C(CH3)COOCH2(CF2)3F
CH2=C(H)COOCH2(CF2)4H
CH2=C(CH3)COOCH2(CF2)4H
CH2=C(H)COOCH2(CF2)F
CH2=C(CH3)COOCH2(CF2)F
CH2=C(H)COO(CH2)2(CF2)8F
CH2=C(CH3)COO(CH2)2(CF2)8F
CH2=C(H)COOCH2CF(CF3)OCF2(CF3)O(CF2)4F
CH2=C(CH3)COOCH2CF(CF3)OCF2(CF3)O(CF2)4F
(CF3)2(CO2CF═CF).