On-press developable negative-working imageable elements
View Patent ↗The present invention relates to negative-working imageable elements that can be used for the manufacture of printing plates. These imageable elements can be developed on on-press by the action of a lithographic printing ink used in combination with either water or a fountain solution. The imageable elements comprise an imageable layer that is not removable in water or fountain solution alone. The imageable layer includes a free radically polymerizable compound, a free radical initiator composition, an infrared radiation absorbing compound, and a polymeric binder comprising poly(alkylene oxide) pendant groups, and preferably additionally pendant cyano groups.
1. A method of providing a lithographic printing plate comprising:
A) imagewise exposing an on-press developable, negative-working imageable element to provide an imaged element with an imaged layer containing both exposed regions and non-exposed regions,
B) prior or subsequently to step A, mounting said imageable element onto a lithographic printing press,
C) after steps A and B, contacting said imaged layer on-press with water or a fountain solution but not a lithographic printing ink for sufficient time to swell said non-exposed regions of said imaged layer but leaving said non-exposed regions of said imaged layer substantially intact on said substrate,
D) contacting said imaged layer with swollen non-exposed regions simultaneously wit water or fountain solution and a lithographic printing ink to substantially remove said non-exposed regions only, and
E) simultaneously with or subsequently to step D, using said imaged element to print an image on a receiver material,
said on-press developable negative-working imageable element comprising an infrared radiation imageable layer on a substrate, said imageable layer comprising:
a free radically polymerizable component,
a free radical initiator composition,
an infrared radiation absorbing compound, and
a polymer binder, wherein said polymeric binder comprises a polymer backbone comprising recurring units having pendant (alkylene glycol) side chains and is at least in part, in particulate form,
said imageable layer being completely removable prior to irradiation only when contacted, sequentially or simultaneously, with either water or a fountain solution and a lithographic printing ink.
2. The method of claim 1 wherein said pendant (alkylene glycol) side chains have a number average molecular weight of at least 300 and up to 10,000.
3. The method of claim 1 wherein said polymeric binder further comprises recurring units having pendant cyano groups.
4. The method of claim 1 wherein said free radically polymerizable component or said infrared radiation absorbing compound is insoluble in water or fountain solution alone.
5. The method of claim 1 wherein said imageable element further comprising a colorant that is insoluble in water or fountain solution alone.
6. The method of claim 1 wherein said free radical initiator composition comprises an onium salt.
7. The method of claim 6 wherein said free radical initiator composition comprises an iodonium borate.
8. The method of claim 6 wherein said free radical initiator composition comprises a diaryliodonium tetrasrylborate.
9. The method of claim 1 wherein said imaging is carried out by an IR laser at a wavelength of from about 700 to about 1200 nm.
10. A method of providing a lithographic printing plate comprising:
A) imagewise exposing an on-press developable. negative-working imageable element to provide an imaged element with an imaged layer containing both exposed regions and non-exposed regions,
B) prior or subsequently to step A, mounting said imageable element onto a lithographic printing press,
C) after steps A and B, contacting said imaged layer on-press with a lithographic printing ink but not water or a fountain solution,
D) contacting said imaged layer with both water or fountain solution and a lithographic printing ink to substantially remove said non-exposed regions only, and
E) simultaneously with or subsequently to step D, using said imaged element to print an image on a receiver material,
said on-press developable negative-working imageable element comprising an infrared radiation imageable layer on a substrate, said imageable layer comprising:
a free radically polymerizable component,
a free radical initiator composition,
an infrared radiation absorbing compound, and
a polymer binder,
said imageable layer being completely removable prior to irradiation only when contacted, sequentially or simultaneously, with either water or a fountain solution and a lithographic printing ink.
11. The method of claim 10 wherein said polymeric binder is composed of recurring units comprising pendant (ethylene glycol) units and at least 50 weight % of all recurring units are recurring units comprising pendant cyano groups.
12. The method of claim 10 wherein before exposure to imaging radiation, said imageable layer is incompletely soluble in water or a fountain solution alone.
13. The method of claim 10 wherein said substrate is a grained, phosphoric acid-anodized aluminum-containing substrate.