Polyester stilbene composition
View Patent ↗A copolyester composition comprising units of residues of a) about 1-40 mole % of trans 3,3′, trans 4,4′ stilbene dicarboxylic acid and the combination thereof, b) about 99-60 mole % of cis,trans, and the combination thereof of 1,4 cyclohexane dicarboxylic acid, and c) about 50-100 mole % of cis, trans, and the combination thereof of 1,4-cyclohexane dimethanol. The resulting copolyester may be characterized by its clarity, as well as enhanced heat performance due to the presence of the stilbene moiety.
1. A composition consisting essentially of a miscible blend of:
(A) a copolyester, at least partially crosslinked, consisting of repeating units of residues of
a. from about 1 to about 40 mole % of trans 3,3′ or trans 4,4′-stilbene dicarboxylic acid, based on the total moles of acid units,
b. from about 99 to about 60 mole % of cis, trans, or a combination thereof of 1,4-cyclohexane dicarboxylic acid, based on the total moles of acid units,
c. from 0 to about 40 mole % of terephthalic acid, isophthalic acid, or a combination thereof, based on the total moles of acid units,
d. from about 50 to about 100 mole % of cis, trans, or a combination thereof of 1,4-cyclohexane dimethanol, based on the total moles of diol units,
e. from 0 to about 50 mole % of ethylene glycol, butylene glycol, or a combination thereof, based on the total moles of diol units, and
f. from 0 to about 2 mole % of a branching agent; and
(B) a polymer selected from the group consisting of polycarbonate, copolyestercarbonate, silicone containing polycarbonate, poly(1,4-cyclohexylenedimethylene 1,4-cyclohexanedicarboxylate, polycarbonate/poly(diorganosiloxane)copolymer, 1,3-resorcinol containing polycarbonate copolymer and mixtures thereof.
2. The composition of claim 1 wherein the copolyester has from about 5 to about 30 mole % of the residue of trans 4,4′ stilbene dicarboxylic acid in the copolyester, based on the total moles of acid units.
3. The composition of claim 1 , wherein the copolyester has from 0 to about 25 mole % of the residue of terephthalic acid, isophthalic acid and a combination thereof, based on the total moles of acid units.
4. The composition of claim 1 , wherein the copolyester has from 0 to about 30 mole % of the residues of ethylene glycol, butylene glycol and a combination thereof, based on the total moles of diol units.
5. The composition of claim 1 , wherein the copolyester is clear.
6. A process for preparing the composition of claim 1 , consisting essentially of a miscible blend, wherein the copolyester is mixed with the polymer selected from the group consisting of polycarbonate, copolyestercarbonate, silicone containing polycarbonate, poly(1,4-cyclohexylenedimethylene 1,4-cyclohexanedicarboxylate, polycarbonate/poly(diorganosiloxane)copolymer, 1,3-resorcinol containing polycarbonate copolymer and mixtures thereof, and then the blend is irradiated, thereby forming at least some crosslinked copolyester.
7. A composition consisting essentially of a clear miscible blend of:
(A) a copolyester comprising repeating units of residues of
a. from about 5 to about 30 mole % of trans 3,3′ or trans 4,4′-stilbene dicarboxylic acid, based on the total moles of acid units,
b. from about 95 to about 70 mole % of cis, trans, or a combination thereof of 1,4-cyclohexane dicarboxylic acid, based on the total moles of acid units,
c. from 0 to about 40 mole % of terephthalic acid, isophthalic acid, or a combination thereof, based on the total moles of acid units,
d. from about 50 to about 100 mole % of cis, trans, or a combination thereof of 1,4-cyclohexane dimethanol, based on the total moles of diol units,
e. from 0 to about 50 mole % of ethylene glycol, butylene glycol, or a combination thereof, based on the total moles of diol units, and
f. from 0 to about 2 mole % of a branching agent; and
(B) a polymer selected from the group consisting of bisphenol-A polycarbonate, copolyestercarbonate, silicone containing polycarbonate, poly(1,4-cyclohexylenedimethylene 1,4-cyclohexanedicarboxylate, polycarbonate/poly(diorganosiloxane)copolymer, 1,3-resorcinol containing polycarbonate copolymer and mixtures thereof, wherein the copolyester is at least partially crosslinked.
8. The composition of claim 7 wherein the copolyester comprises from 10 mole % to 30 mole % or trans 4,4′ stilbene dicarboxylic acid, based on the total moles of acid units.
9. The method of claim 6 wherein the copolyester is mixed with a polymer selected from the group consisting of bisphenol-A polycarbonate, copolyestercarbonate, silicone containing polycarbonate, poly(1,4-cyclohexylenedimethylene 1,4-cyclohexanedicarboxylate, polycarbonate/poly(diorganosiloxane)copolymer, 1,3-resorcinol containing polycarbonate copolymer and mixtures thereof, and then the blend is irradiated, thereby forming at least some crosslinked copolyester.