Preparation of cellulose ether products of increased viscosity and fineness
View Patent ↗The present invention relates to a process for preparing cellulose ether products which is characterized in that superabsorbent polymers (SAPs) are dried and milled, or mill-dried, conjointly with moist cellulose ether and also to the cellulose ether products resulting from this process.
1. A process for preparing cellulose ethers of increased viscosity and increased fineness comprising:
washing a crude cellulose ether to obtain a water-moist cellulose ether,
mixing the water-moist cellulose ether, said water-moist cellulose ether having a moisture content in the range from 25% to 75% by weight, with 0.5% to 2.0% by weight based on the dry cellulose ether of a pulverulent superabsorbent polymer (SAP) to produce a millbase, and
then drying and milling or mill-drying the millbase, whereby the fraction of produced cellulose ether passing through a 0.063 mm sieve is increased by more than 15% relative to a control cellulose ether prepared in the absence of an SAP.
2. The process according to claim 1 , wherein the water-moist cellulose ether has a moisture content in the range from 45% to 65% by weight.
3. The process according to claim 1 , wherein the millbase has a moisture content in the range from 45% to 80% by weight based on the total weight of the millbase.
4. The process according to claim 1 , wherein the millbase has a moisture content in the range from 60% to 75% by weight based on the total weight of the millbase.
5. The process according claim 1 , wherein the cellulose ether is selected from methyl cellulose or methylhydroxyalkyl cellulose.
6. The process according to claim 1 , wherein the cellulose ether is methylhydroxyalkyl cellulose having a DS (methyl) of from 0.9 to 3 and an MS (hydroxyalkyl) of from 0.05 to 1.
7. The process according to claim 6 , wherein the cellulose ether is methylhydroxyalkyl cellulose having a DS (methyl) of from 1.1 to 1.8 and an MS (hydroxyalkyl) of from 0.10 to 0.7.
8. The process according to claim 7 , wherein the cellulose ether is methylhydroxyalkyl cellulose having a DS (methyl) of from 1.3 to 1.6 and an MS (hydroxyalkyl) of from 0.25 to 0.50.
9. The process according claim 1 , wherein the SAP is selected from crosslinked partially neutralized polyacrylic acids, (partial) hydrolysates of starch-acrylonitrile graft copolymers, (partially) neutralized starch-acrylic acid graft copolymers, (partially) hydrolysed vinyl acetate-acrylic ester copolymers, (partially) hydrolysed acrylonitrile or acrylamide copolymers, crosslinked products of such hydrolysates and polymers of crosslinked cationic monomers.
10. The process according to claim 1 , wherein 0.6% to 1.2% by weight based on the dry cellulose ether of a pulverulent SAP is used.
11. The process according to claim 2 , wherein 0.6% to 1.2% by weight based on the dry cellulose ether of a pulverulent SAP is used.
12. The process according to claim 3 , wherein 0.6% to 1.2% by weight based on the dry cellulose ether of a pulverulent SAP is used.
13. The process according to claim 5 , wherein 0.6% to 1.2% by weight based on the dry cellulose ether of a pulverulent SAP is used.
14. The process according to claim 9 , wherein 0.6% to 1.2% by weight based on the dry cellulose ether of a pulverulent SAP is used.
15. The process according to claim 6 , wherein 0.6% to 1.2% by weight based on the dry cellulose ether of a pulverulent SAP is used.
16. The process according to claim 8 , wherein 0.6% to 1.2% by weight based on the dry cellulose ether of a pulverulent SAP is used.