Method and composition for coating mat and articles produced therewith
View Patent ↗A coated glass mat comprises a glass mat substrate having non-woven glass fibers and a coating which essentially uniformly penetrates the glass mat substrate to desired fractional thickness of the coated glass mat. The coating imparts a tensile strength to the coated glass mat which on average is at least 1.33 times greater than the tensile strength of the glass mat substrate without the coating. In example embodiments, penetration of the coating into the glass mat substrate preferably extends to a depth of from twenty five percent of a thickness of the coated glass mat to seventy five percent of the thickness of the coated glass mat. Moreover, a non-coated thickness of the coated glass mat is sufficiently thick for bonding purposes with, e.g., a gypsum slurry or other core materials such as thermoplastic or thermosetting plastics. The coating has a porosity in a range of from 1.3 CFM to 5.0 CFM, e.g., the coating comprises a coating blend which provides the coated glass mat with a porosity sufficient to allow water vapor to escape from a gypsum slurry when heated. The coating is preferably a coating blend comprised of water, latex binder, inorganic pigment, and inorganic binder.
1. A coated glass mat comprising:
a glass mat substrate having non-woven glass fibers; and
a coating comprising latex binder and inorganic pigment,
said coating being present in an amount of about 61 lbs/MSF to about 75 lbs/MSF and being only partially permeated into said substrate while also imparting a tensile strength to the coated glass mat which on average is at least 1.33 times greater than the tensile strength of the glass mat substrate without the coating, wherein the coating comprises a coating blend which provides the coated glass mat with a porosity sufficient to allow water vapor to escape from a gypsum slurry when heated.
2. The coated glass mat of claim 1 , wherein the coating further comprises an inorganic binder.
3. The coated glass mat of claim 1 , wherein said non-woven glass mat weighs between about twelve pounds per thousand square feet and about fifty pounds per thousand square feet.
4. The coated glass mat of claim 1 , wherein the glass mat substrate before coating weighs about fourteen and a half (14.5) pounds per thousand square feet and wherein after coating the coated glass mat has a tensile strength which on average is greater than one hundred twenty pounds per three-inch width.
5. The coated glass mat of claim 1 , wherein the glass mat substrate before coating weighs about twenty-six and a half (26.5) pounds per thousand square feet and wherein after coating the coated glass mat has a tensile strength which on average is greater than two hundred twenty pounds per three-inch width.
6. The coated glass mat of claim 1 , wherein penetration of the coating into the glass mat substrate extends a depth of from twenty five percent of a thickness of the coated glass mat to seventy five percent of the thickness of the coated glass mat.
7. The coated glass mat of claim 1 , wherein the coating uniformly penetrates the glass mat substrate to a desired fractional thickness of the coated glass mat.