Nanocomposite particle and process of preparing the same
View Patent ↗A nanocomposite particle, its use as a catalyst, and a method of making it are disclosed. The nanocomposite particle comprises titanium dioxide nanoparticles, metal oxide nanoparticles, and a surface stabilizer. The metal oxide nanoparticles are formed hydrothermally in the presence of the titanium dioxide nanoparticles. The nanocomposite particle is an effective catalyst support, particularly for DeNO x catalyst applications.
1. A nanocomposite particle comprising:
(a) titanium dioxide nanoparticles, wherein the titanium dioxide nanoparticles have an average size of less than about 50 nm and a surface area of greater than or equal to about 20 m 2 /g;
(b) metal oxide nanoparticles selected from the group consisting of zirconium dioxide, cerium dioxide, tin oxide, niobium oxide and mixtures and combinations thereof, wherein the metal oxide nanoparticles have an average size of less than about 50 nm; and
(c) a surface stabilizer selected from the group consisting of silicon dioxide, aluminum oxide, phosphorus pentoxide, aluminum silicate and aluminum phosphate,
wherein the metal oxide nanoparticles are formed by hydrothermally treating an amorphous hydrated metal oxide in the presence of the titanium dioxide nanoparticles, and wherein the nanocomposite particle has an average pore volume between the titanium dioxide nanoparticles and the metal oxide nanoparticles of greater than about 0.3 cm 3 /g.
2. The nanocomposite particle of claim 1 wherein the titanium dioxide nanoparticles are predominantly anatase.
3. The nanocomposite particle of claim 1 wherein the metal oxide nanoparticles are zirconium dioxide.
4. The nanocomposite particle of claim 1 comprising 50 to 95 weight percent titanium dioxide nanoparticles, 2 to 48 weight percent metal oxide nanoparticles, and 2 to 20 weight percent surface stabilizer.
5. The nanocomposite particle of claim 1 having a surface area greater than 60 m 2 /g after being calcined at 800° C. for 6 hours.
6. The nanocomposite particle of claim 1 , wherein the average pore volume between the titanium dioxide nanoparticles and the metal oxide nanoparticles is in a range of from about 0.3 cm 3 /g to about 0.8 cm 3 /g.
7. A catalyst comprising the nanocomposite particle of claim 1 and at least one metal component comprising a metal selected from the group consisting of platinum, gold, silver, palladium, copper, tungsten, molybdenum, vanadium, iron, rhodium, nickel, manganese, chromium, cobalt, and ruthenium.
8. The catalyst of claim 7 wherein the metal component is selected from the group consisting of tungsten trioxide and vanadium pentoxide.
9. The catalyst of claim 8 comprising 0.1 to 10 weight percent vanadium pentoxide and 4 to 20 weight percent tungsten trioxide.