Low density drywall
A thin drywall board that includes a gel coat, at least one polymer/gypsum layer, and a wet glass fiber layer is provided. The gel coat is formed of a gel coat composition that includes a water dispersible polymer, gypsum, and optionally a crosslinking agent and/or a coupling agent. The polymer/gypsum layer is formed of a matrix composition that includes a water dispersible polymeric resin and gypsum. Components including melamine formaldehyde, a filler material, coupling agents, acetic acid, an accelerator, and/or a hardener may also be added to the matrix composition. The wet glass fiber layer is preferably a glass fiber mat. The combination of the water dispersible polymeric resin and the gypsum in the matrix composition have a synergistic effect that creates a thin drywall board that is water resistant, fire resistant, and has improved mechanical properties. A method of forming the inventive thin drywall boards is also provided.
1 . A lightweight, thin drywall board comprising:
a gel coat, said gel coat forming an exterior, viewable surface;
a first polymer/gypsum layer positioned on said gel coat, said polymer/gypsum layer being formed of a matrix composition including:
one or more water dispersible polymeric resins; and
gypsum; and
a first glass fiber mat layer positioned on said first polymer/gypsum layer to form an external surface opposing said gel coat.
2 . The thin drywall board of claim 1 , wherein a reinforcement layer is positioned between said first polymer/gypsum layer and said first glass fiber mat layer, said reinforcement layer including a second glass fiber mat layer located next to said first polymer/gypsum layer and a second polymer/gypsum layer located next to said first glass fiber mat layer.
3 . The thin drywall board of claim 2 , wherein a second reinforcement layer including a third glass fiber mat layer and a third polymer/gypsum layer is positioned adjacent to said first reinforcement layer such that said glass fiber mat layers and said polymer/gypsum layers alternate.
4 . The thin drywall board of claim 3 , wherein said gel coat has a surface selected from the group consisting of a smooth surface and a textured surface.
5 . The thin drywall board of claim 3 , wherein said gel coat is formed of a gel coat composition including:
at least one water soluble polymer;
gypsum; and
a crosslinking polymer or an accelerating agent.
6 . The thin drywall board of claim 5 , wherein said gel coat composition includes melamine formaldehyde as a crosslinking polymer.
7 . The thin drywall board of claim 3 , wherein said matrix composition further comprises at least one member selected from the group consisting of a filler material, at least one coupling agent, an organic acid, an accelerator, a hardener and a crosslinking polymer.
8 . The thin drywall board of claim 3 , wherein said drywall board is formed as a continuous sheet that is larger in size than conventional drywall boards.
9 . The thin drywall board of claim 5 , wherein said gel coat composition further comprises at least one member selected from the group consisting of a coupling agent and a hardening agent.
10 . A composite board for use as a construction material comprising:
a gel coat, said gel coat forming an exterior, viewable surface; and
multiple stratums formed of polymer/gypsum layers alternating with glass fiber mat layers such that a first polymer/gypsum layer is positioned next to said gel coat and a last glass fiber mat forms an external surface opposing said gel coat.
11 . The composite board of claim 8 , wherein said polymer/gypsum layer is formed of a matrix composition including:
one or more water dispersible polymeric resins; and
gypsum; and
12 . The composite board of claim 9 , wherein said matrix composition further comprises at least one member selected from the group consisting of a filler material, at least one coupling agent, an organic acid, an accelerator, a hardener and a crosslinking polymer.
13 . The composite board of claim 9 , wherein said gel coat is formed of a gel coat composition including:
at least one water soluble polymer;
gypsum; and
a crosslinking polymer or an accelerating agent.
14 . The composite board of claim 11 , wherein said gel coat composition further comprises at least one member selected from the group consisting of a coupling agent and a hardening agent.
15 . The composite board of claim 9 , wherein composite board includes three or more of said glass fiber mat layers and forms a structural drywall board, sheathing, or a lumber board.
16 . The composite board of claim 13 , wherein said composite board contains three of said polymer/gypsum layers and three of said glass fiber mat layers to form a drywall board that is equal to or greater than the size of conventional drywall boards.
17 . A method of forming a composite board for use as a construction material comprising the steps of:
placing a gel coat composition on a releasable surface, said releasable surface being smooth or textured;
permitting said gel coat composition to harden and form a gel coat; and
alternately layering a polymer/gypsum layer and a glass fiber mat layer on said gel coat to form a composite board; and
wherein one of said polymer/gypsum layers is positioned adjacent to said gel coat and one of said glass fiber mat layers forms an external opposing surface to said gel coat.
18 . The method of claim 15 , wherein said placing step includes an application method selected from the group consisting of spraying, rolling and uniformly metering said gel coat composition onto said releasable surface.
19 . The method of claim 15 , wherein said gypsum/polymer layers are formed of a matrix composition comprising:
one or more water dispersible polymeric resins; and
gypsum.
20 . The method of claim 17 , further comprising the step of removing the composite board from said releasable surface.
21 . The method of claim 17 , wherein said gel coat composition comprises:
at least one water soluble polymer;
gypsum; and
a crosslinking polymer or an accelerating agent.
22 . The method of claim 19 , wherein said gel coat composition further comprises at least one member selected from the group consisting of a coupling agent and a hardening agent.