Reflector having high light diffusion
The invention pertains to a reflector comprising a substrate capable of reflecting light, characterized in that the reflector exhibits a gloss of less than 10% as determined when a light source is projected on the surface of the reflector at 60 degree. The reflector of the invention allows the light to be reflected uniformly and possesses a high reflectivity.
1. A reflector comprising:
an opaque substrate that is capable of reflecting light and comprises at least one layer of a polymeric resin, in which the substrate is coated with a coating layer having a convex-concave micro-structure and containing particles with a diameter in the range of 1 μm to 50 μm and a binder,
wherein the amount of the particles is in the range of 20 to 200 weight % based on the weight of the binder, and the reflector exhibits a gloss of less than 10% as determined according to an ASTM D523 standard method at an incidence angle of 60 degrees.
2. The reflector according to claim 1 , wherein the particles are organic particles, inorganic particles, or a mixture thereof.
3. The reflector according to claim 2 , wherein the organic particles are selected from the group consisting of acrylic resin, styrene resin, urethane resin, silicone resin, and a mixture thereof.
4. The reflector according to claim 2 , wherein the inorganic particles are selected from the group consisting of zinc oxide, silicon dioxide, titanium dioxide, zirconia, aluminium oxide, zinc sulfide, barium sulfate, and a mixture thereof.
5. A reflector for use in a backlight module, comprising:
an opaque substrate that is capable of reflecting light and contains at least one layer of a polyester resin, in which the substrate is coated with a coating layer having a convex-concave micro-structure and containing particles with a diameter in the range of 1 μm to 50 μm and a binder,
wherein the amount of the particles is in the range of 20 to 200 weight % based on the weight of the binder, and the reflector exhibits a reflectivity of greater than 97% in a visible wavelength range of 400 μm to 780 μm and a gloss of less than 10% as determined according to an ASTM D523 standard method at an incidence angle of 60 degrees.
6. The reflector according to claim 5 , wherein the particles are organic particles.
7. The reflector according to claim 6 , wherein the particles are selected from the group consisting of acrylic resin, styrene resin, urethane resin, silicone resin, and a mixture thereof.
8. A light diffusion reflector for use in a direct type backlight module, comprising:
a substrate that is capable of reflecting light and contains at least one layer of polyethylene terephthalate, in which the substrate is coated with a coating layer having a convex-concave micro-structure and containing organic particles with a diameter in the range of 1 μm to 50 μm and a binder,
wherein the amount of the organic particles is in the range of 30 to 200 weight % based on the weight of the binder, and the reflector exhibits a reflectivity of greater than 97% in a visible wavelength range of 400 μm to 780 μm and a gloss of less than 10% as determined according to an ASTM D523 standard method at an incidence angle of 60 degrees.
9. The light diffusion reflector according to claim 8 , wherein the organic particles have a diameter in the range of 1 μm to 10 μm.
10. The light diffusion reflector according to claim 9 , wherein the organic particles are silicone resin particles.
11. The light diffusion reflector according to claim 8 , wherein the binder is selected from the group consisting of acrylic resin, polyamide resin, epoxy resin, fluoro resin, polyimide resin, polyurethane resin, alkyd resin, polyester resin, and a mixture thereof.
12. The light diffusion reflector according to claim 8 , wherein the amount of the organic particles is in the range of 30 to 60 weight % based on the weight of the binder.
13. The light diffusion reflector according to claim 8 , wherein the coating further comprises inorganic substances.