Oligomeric lactide macromer based copolymer and a process for the preparation thereof
View Patent ↗A macromer based novel copolymer comprising an acrylate or methacrylate ester of low molecular weight oligomeric lactide copolymerized with basic monomer is provided. These copolymers show unusual dissolution behavior in that they are soluble over a wide range of pH from 1.8 to 7.4. This unexpected solubility behavior can be exploited to develop pharmaceutical dosage forms.
1. An oligomeric lactide macromer based copolymer having a general formula
[A (x) B (y) ] n
wherein A is an oligomeric lactide macromer selected from the group consisting of oligo (lactide) acrylate and oligo (lactide) methacrylate and having a degree of polymerization of from 2 to 10; B is a basic monomer; selected from the group consisting of dimethyl amino ethyl methacrylate, dimethyl amino ethyl acrylate, diethyl amino ethyl methacrylate, diethyl amino ethyl acrylate, piperidine ethyl methacrylate and 2-tert-butyl amino ethyl methacrylate; x is from 1 to 4; y is from 3 to 7; and n is from 1 to 5, wherein a molecular weight of the oligomeric lactide macromer is from 500 to 1000, wherein the copolymer has a molecular weight of from 1000 to 5000, and wherein the copolymer is soluble in an aqueous medium at a pH of from 1.8 to 7.4.
2. The copolymer of claim 1 , wherein a content of oligomeric lactide macromer is from 25% w/w to 90% w/w of the copolymer.
3. The copolymer of claim 1 , wherein a content of basic monomer is from 10% w/w to 75% w/w of the copolymer.
4. A process for the preparation of an oligomeric lactide macromer based copolymer,
which comprises:
preparing a solution of an oligomeric lactide macromer selected from the group consisting of oligo (lactide) acrylate and oligo (lactide) methacrylate and having a degree of polymerization of from 2 to 10 and basic monomer selected from the group consisting of dimethyl amino ethyl methacrylate, dimethyl amino ethyl acrylate, diethyl amino ethyl methacrylate, diethyl amino ethyl acrylate, piperidine ethyl methacrylate and 2-tert-butyl amino ethyl methacrylate; in an organic solvent;
adding a free radical initiator to the solution and heating it to a temperature of from 50 to 75° C., for a period of from 16 to 24 hours, whereby a reaction mixture is obtained;
concentrating the reaction mixture by removing organic solvent, at a reduced pressure; and
precipitating the concentrated reaction mixture in water to recover the oligomeric lactide macromer based copolymer having a general formula:
[A (x) B (y) ] n
wherein A is the oligomeric lactide macromer; B is the basic monomer; x is from 1 to 4; y is from 3 to 7; and n is from 1 to 5, wherein the oligomeric lactide macromer has a molecular weight of from 500 to 1000, wherein the copolymer has a molecular weight of from 1000 to 5000, and wherein the copolymer is soluble in an aqueous medium at a pH of from 1.8 to 7.4.
5. The process of claim 4 , wherein the organic solvent is selected from the group consisting of chlorinated hydrocarbon, alcohol, ester, ketone, formamide, tetrahydrofuran, dioxane, and dimethyl sulfoxide.
6. The process of claim 4 , wherein the free radical initiator is selected from the group consisting of azo compound, peroxide, hydroperoxide, peracid, and perester.
7. The process of claim 6 , wherein the azo compound is selected from the group consisting of azo-bis-cyano-valeric acid, azo-bis-biphenyl methane, azo-bis-methyl isobutyrate, and azo-bis-isobutyronitrile.
8. The process of claim 4 , wherein the copolymer has a content of oligomeric lactide macromer of from 25% w/w to 90% w/w of the copolymer.
9. The process of claim 4 , wherein the copolymer has a content of basic monomer of from 10% w/w to 75% w/w of the copolymer.