Aging-resistant copolymers comprising polyamide blocks and polyether blocks
View Patent ↗The present invention relates to compositions based on a copolymer comprising homo- or copolyamide polyamide blocks (PA blocks), with the exclusion of completely aromatic PA blocks, and polyether blocks comprising: a) 500 to 10 000 ppm of at least one phenolic antioxidant; b) 0 to 5000 ppm of at least one antioxidant based on phosphorus or based on sulphur; c) 0 to 5000 ppm of at least one UV absorber; d) 200 to 3000 ppm of at least one methylated hindered amine light stabilizer or HALS and/or 200 to 1300 ppm of at least one nonmethylated HALS.
1. A copolymer composition comprising:
a copolymer of polyamide blocks, and polyether blocks, wherein the copolymer does not comprise completely aromatic polyamide blocks, the copolymer composition further comprising
a) 3,000 to 8,000 ppm of at least one hindered phenolic antioxidant, wherein the at least one hindered phenolic antioxidant comprises pentaerythritol tetrakis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate);
b) 1,000 to 5,000 ppm of at least one antioxidant selected from the group consisting of bis(2,6-di-ter-butyl-4-methylphenyl)pentaerythritol-di-phosphite- and bis(2,4 dicumylphenyl)pentaerythritol diphosphate;
c) 1,000 to 5,000 ppm of at least one UV absorber, wherein the at least one UV absorber comprises N-(2-ethoxyphenyl)-N′-(4-ethylphenyl)-ethylene diamide;
d) 400 to 1,000 ppm of a methylated hindered amine light stabilizer and no nonmethylated HALS, wherein the methylated hindered amine light stabilizer is selected from the group consisting of tetrakis(1,2,2,6,6-pentamethyl-4-piperidyl) 1,2,3,4-butanetetracarboxytate and N′,N′″-[1,2-ethane-diyl-bis[[[4,6-bis-[butyl-(1,2,2,6,6-pentamethyl-4-piperidinyl)amino]-1,3,5-triazine-2-yl]imino]-3,1-propanediyl]]bis-[N′,N″-dibutyl-N′,N″-bis(1,2,2,6,6-penta methyl-4-piperidinyl)-1,3,5-triazine-2,4,6-triamine, and a mixture of bis(1,2,2,6,6-pentamethyl-4-piperidyl)sebacate and methyl-1,2,2,6,6-pentamethyl-4-piperidyl sebecate.
2. The copolymer composition according to claim 1 , wherein the level of the at least one hindered phenolic antioxidant (a) is between 3,000 and 6,000 ppm.
3. The copolymer composition according to claim 1 , wherein the level of the at least one antioxidant (b) is between 1,000 and 2,000 ppm.
4. The copolymer composition according to claim 1 , wherein the level of the at least one antioxidant (b) is between 1,200 and 1,700 ppm.
5. The copolymer composition according to claim 1 , wherein the level of the at least one UV absorber (c) is between 1,000 and 2,000 ppm.
6. The copolymer composition according to claim 1 , wherein the level of the at least one UV absorber (c) is between 1,200 and 1,700 ppm.
7. The copolymer composition according to claim 1 , wherein the polyamide blocks are polyamide 12, polyamide 11 or polyamide 6 blocks and the polyether blocks are polytetramethylene glycol, polyethylene glycol or polypropylene glycol blocks.
8. The copolymer composition according to claim 1 , wherein the polyether blocks are 5 to 85% by weight of the copolymer.
9. The copolymer composition according to claim 1 , wherein the methylated hindered amine light stabilizer has a molecular weight between 500 and 1,000 g/mol.
10. An article comprising the copolymer composition according to claim 1 .
11. The article of claim 10 , wherein said article is a shoe sole.
12. A copolymer composition comprising:
a copolymer of polyamide blocks, and polyether blocks, wherein the copolymer does not comprise completely aromatic polyamide blocks, the copolymer composition further comprising stabilizers consisting of:
a) 3,000 to 8,000 ppm of at least one hindered phenolic antioxidant, wherein the at least one hindered phenolic antioxidant comprises pentaerythritol tetrakis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate);
b) 1,000 to 5,000 ppm of at least one antioxidant based on phosphorus, wherein the at least one antioxidant based on phosphorus is selected from the group consisting of bis(2,6-di-ter-butyl-4-methylphenyl)pentaerythritol-di-phosphite and bis(2,4-dicumylphenyl)pentaerythritol diphosphate;
c) 1,000 to 5,000 ppm of at least one UV absorber, wherein the at least one UV absorber comprises N-(2-ethoxyphenyl)-N′-(4-ethylphenyl)-ethylene diamide; and
d) 400 to 1,000 ppm of single methylate hindered amine light stabilizer and no nonmethylated hindered amine light stabilizer, wherein the methylated hindered amine light stabilizer is selected from the group consisting of tetrakis(1,2,2,6,6-pentamethyl-4-piperidyl) 1,2,3,4-butanetetracarboxylate, N,N″-[1,2-ethane-diyl-bis[[[4,6-bis-[butyl-(1,2,2,6,6-penta methyl-4-piperidinyl)amino]-1,3,5-triazine-2-yl]imino]-3,1-propanediyl]]bis-[N′,N″-dibutyl-N,N″-bis(1,2,2,6,6-pentamethyl-4-piperidinyl)-1,3,5-triazine-2,4,6-triamine, and a mixture of bis(1,2,2,6,6-pentamethyl-4-piperidyl)sebacate and methyl-1,2,2,6,6-pentamethyl-4-piperidyl sebecate.