High shear pressure sensitive adhesive composition
View Patent ↗A hot melt pressure sensitive adhesive composition includes ABA block copolymer(s), a midblock resin, a plasticizer, and optionally, an endblock resin. The A block is derived from styrene and B block is derived from butadiene or its hydrogenated version. The block copolymer(s) has an average styrene content of from about 15% to about 35%, an average diblock content of no less than about 20%, and an average solution viscosity of less than about 1,000 cps.
1. A hot melt pressure sensitive adhesive composition comprising:
ABA block copolymer(s), said A block being styrene and said B block being butadiene or the hydrogenated version thereof, said block copolymer(s) having an average styrene content of from about 15% to 35%, an average diblock content of no less than about 20%, and an average solution viscosity of less than 1,000 cps when tested at 25° C. in a 25 weight % solution of toluene;
a midblock resin;
a plasticizer; and
an end block resin,
wherein said adhesive has a melt viscosity of no greater than about 30,000 cps at 350° F., and wherein said adhesive exhibits static shear adhesion of at least about 5 hours at 40° C.
2. The hot melt adhesive composition of claim 1 , wherein said end block resin has a softening point of no less than about 140° C.
3. The hot melt adhesive composition of claim 1 , wherein said midblock resin has a softening point of from about 100° C. to about 140° C.
4. The hot melt adhesive composition of claim 1 , wherein said composition comprises from about 25% to about 40% by weight of said block copolymer(s).
5. The hot melt adhesive composition of claim 1 , wherein said composition comprises from about 3% to about 12% by weight of said end block resin.
6. The hot melt adhesive composition of claim 1 , wherein said composition comprises from about 40% to about 60% by weight of said midblock resin.
7. The hot melt adhesive composition of claim 1 , wherein said plasticizer is liquid plasticizer.
8. The hot melt adhesive composition of claim 1 , wherein said composition comprises from about 8% to about 20% by weight of said plasticizer.
9. The hot melt adhesive composition of claim 1 , wherein said adhesive composition exhibits static shear adhesion of at least about 10 hours at 40° C.
10. The hot melt adhesive composition of claim 1 , further comprising a polypropylene polymer.
11. The hot melt adhesive composition of claim 1 , wherein said adhesive has a melt viscosity of no greater than about 25,000 cps at 350° F.
12. The hot melt adhesive composition of claim 1 , wherein said adhesive has a melt viscosity of no greater than about 15,000 cps at 350° F.
13. An article comprising:
a substrate; and
a hot melt adhesive composition of claim 1 disposed on said substrate.
14. The article of claim 13 , wherein said substrate is chosen from polyethylene, polypropylene, polyethylene tetraphthalate, woven or nonwoven polyolefins, paper, foam, vinyl, foil, chip board, engineered wood, or the combinations thereof.
15. The article of claim 13 , wherein said article is a fastening tape for a disposable article.
16. The article of claim 13 , wherein said article comprises diapers, and incontinence garments.
17. The article of claim 13 , wherein said article comprises transfer tapes, box closure, and carton sealing.
18. A method of constructing the article of claim 13 , comprising contacting said substrate with said adhesive composition.
19. The hot melt adhesive composition of claim 1 , wherein said composition has an average diblock content of no less than about 75%.
20. A hot melt pressure sensitive adhesive composition comprising:
ABA block copolymer(s), said A block being styrene and said B block being butadiene or the hydrogenated version thereof, said block copolymer(s) having an average styrene content of from about 15% to about 35%, an average diblock content of no less than about 50%, and an average solution viscosity of less than 1,000 cps when tested at 25° C. in a 25 weight % solution of toluene;
a midblock resin;
a plasticizer; and
an end block resin,
wherein said adhesive has a melt viscosity of no greater than about 30,000 cps at 350° F., and wherein said adhesive exhibits static shear adhesion of at least about 5 hours at 40° C.