Cold-box binders containing an epoxy resin, acrylate, and isooctyl tallate
View Patent ↗This invention relates to foundry binder systems, which will cure in the presence of sulfur dioxide and a free radical initiator, comprising (a) an epoxy resin; (b) an acrylate; (c) an alkyl ester of a fatty acid, wherein the alkyl group of the ester is an aliphatic hydrocarbon having from 4 to 8 carbon atoms, preferably butyl tallate; and (d) an effective amount of a free radical initiator. The foundry binder systems are used for making foundry mixes. The foundry mixes are used to make foundry shapes (such as cores and molds) which are used to make metal castings, particularly ferrous castings.
1. A foundry binder system, which cures in the presence of sulfur dioxide and a free radical initiator, comprising:
(a) 20 to 70 parts by weight of an epoxy resin;
(b) 1 to 50 parts by weight of an acrylate;
(c) 1 to 30 parts of isooctyl tallate; and
(d) from 10 to 25 parts by weight of a peroxide,
wherein (a), (b), and (c) are separate components or mixed with another of said components, provided (b) is not mixed with (d), and where said parts by weight are based upon 100 parts of binder.
2. The binder system of claim 1 wherein the epoxy resin comprises an epoxy resin derived from bisphenol A.
3. The binder system of claim 2 wherein the epoxy resin has an epoxide equivalent weight of about 165 to 200 grains per equivalent.
4. The binder system of claim 3 wherein the acrylate is a monomer.
5. The binder system of claim 4 wherein the acrylate is trimethylolpropane triacrylate and the peroxide is a hydroperoxide.
6. The binder system of claim 5 wherein the hydroperoxide is cumene hydroperoxide.
7. The foundry binder system of claim 6 wherein the amount of epoxy resin is from 40 to 65 parts by weight; the amount of acrylate is from 5 to 30 parts by weight; the amount of isooctyl tallate is from 5 to 25 parts by weight; and the amount of free radical initiator is from 15 to 20 parts by weight.
8. A foundry mix comprising:
(a) a major amount of foundry aggregate;
(b) an effective bonding amount of the foundry binder system of claim 1 , 2 , 3 , 4 , 5 , 6 , or 7 .
9. A cold-box process for preparing a foundry shape comprising:
(a) introducing the foundry mix of claim 8 into a pattern; and
(b) curing with gaseous sulfur dioxide.
10. A foundry shape prepared in accordance with claim 9 .