Preparation of bulk superhard B-C-N nanocomposite compact
View Patent ↗Bulk, superhard, B—C—N nanocomposite compacts were prepared by ball milling a mixture of graphite and hexagonal boron nitride, encapsulating the ball-milled mixture at a pressure in a range of from about 15 GPa to about 25 GPa, and sintering the pressurized encapsulated ball-milled mixture at a temperature in a range of from about 1800-2500 K. The product bulk, superhard, nanocomposite compacts were well sintered compacts with nanocrystalline grains of at least one high-pressure phase of B—C—N surrounded by amorphous diamond-like carbon grain boundaries. The bulk compacts had a measured Vicker's hardness in a range of from about 41 GPa to about 68 GPa.
1. A process for preparing a bulk, superhard, nanocomposite compact, comprising:
(a) ball milling a mixture consisting essentially of graphite and hexagonal boron nitride to produce a ball-milled mixture comprising amorphous boron nitride, nanocrystalline boron nitride, or mixtures thereof, the ball-milled mixture further comprising amorphous carbon, nanocrystalline graphitic carbon, or mixtures thereof;
(b) encapsulating the ball-milled mixture; and thereafter
(c) subjecting the now encapsulated ball-milled mixture to a pressure in a range of from about 15 GPa to about 25 GPa; and thereafter
(d) sintering the pressurized, encapsulated ball-milled mixture at a temperature in a range of from about 1800 K to about 2500 K for a period of time sufficient to convert the pressurized encapsulated ball-milled mixture into a bulk, superhard nanocomposite compact consisting essentially of nanocrystalline grains of at least one ternary phase of B—C—N surrounded by amorphous diamond-like carbon grain boundaries.
2. The process of claim 1 , wherein the step of ball milling a mixture consisting essentially of graphite and hexagonal boron nitride involves ball milling a mixture that consists essentially of about 1 part graphite to about 1 part hexagonal boron nitride.
3. The process of claim 1 , wherein the step of ball milling a mixture consisting essentially of graphite and hexagonal boron nitride involves ball milling a mixture that consists essentially of about 2 parts graphite to about 1 part hexagonal boron nitride.
4. The process of claim 1 , wherein the step of ball milling a mixture consisting essentially of graphite and hexagonal boron nitride involves ball milling a mixture that consists essentially of 4 parts graphite to about 1 part hexagonal boron nitride.
5. The process of claim 1 , wherein step (d) comprises sintering the pressurized, encapsulated ball-milled mixture at a temperature of about 2000 K to about 2500 K.
6. The process of claim 1 , wherein step (c) comprises subjecting the encapsulated ball-milled mixture to at a pressure of about 16 GPa.
7. The process of claim 1 , wherein step (c) comprises subjecting the encapsulated, ball-milled mixture to a pressure in a range of from about 20 GPa to about 25 GPa, and step (d) comprises sintering the pressurized, encapsulated ball-milled mixture at a temperature in a range of from about 2000 K to about 2500 K.
8. The process of claim 1 , wherein step (c) comprises subjecting the encapsulated, ball-milled mixture to a pressure in a range of from about 20 GPa to about 25 GPa and step (d) comprises sintering the pressurized, encapsulated ball-milled mixture at a temperature in a range of about 2100 K to about 2400 K.
9. The process of claim 1 , wherein step (c) comprises subjecting the encapsulated, ball-milled mixture to a pressure of about 20 GPa and step (d) comprises sintering the pressurized, encapsulated ball-milled mixture at a temperature in a range of from about 2000-2400 K.
10. The process of claim 1 , wherein step (c) comprises subjecting the encapsulated, ball-milled mixture to at a pressure of about 25 GPa and step (d) comprises sintering the pressurized, encapsulated ball-milled mixture at a temperature in a range of about 2100 K to about 2300 K.
11. The process of claim 1 , wherein the compact has a Vickers hardness in a range of from about 41 GPa to about 69 GPa.
12. The process of claim 1 , wherein the compact has a Vickers hardness in a range of from about 50 GPa to about 68 GPa.
13. The process of claim 1 , wherein the compact has a Vickers hardness in a range of from about 62 GPa to about 58 GPa.
14. The process of claim 1 , wherein the compact has a Vickers hardness of about 68 GPa.