Operating methods for a batch commercial metal coil laminating line

1. An improved commercial batch laminating process for a flat metal substrate comprising:

a. continuously unwinding a coil of said flat metal substrate by controlling the tension and speed of said flat metal substrate,

b. pretreating one or both major surfaces of said flat metal substrate by raising the surface energy of any said major surface to at least 55 dynes,

c. preheating said flat metal substrate to a laminating temperature,

d. pressing a laminating film onto any said pretreated major surface of said flat metal substrate thereby creating a film-metal laminate, wherein each said pretreated major surface of said flat metal substrate may have a different said laminating film,

e. wherein any of said laminating film comprises primarily a thermoplastic polymer,

f. reheating said film-metal laminate to a post treatment temperature,

g. cooling said film-metal laminate to a winding temperature,

h. wherein the threaded length of said flat metal substrate in said commercial batch laminating process is less than 200 feet, and

i. wherein said commercial batch laminating process includes the capability to dynamically trim any laminating film which is wider than said flat metal substrate to substantially the same width as said flat metal substrate.

2. A process according to claim 1 wherein said dynamic trimming comprises a plurality of rotating knives that are positioned relative to the lengthwise edges of said flat metal substrate by an electronic control, wherein the motion of said rotating knives that is perpendicular to the lengthwise direction of said flat metal substrate is less than 1% of the lengthwise speed of said flat metal substrate.

3. A process according to claim 2 wherein two said rotating knives are positioned relative to each lengthwise edge of said flat metal substrate.

4. A process according to claim 2 wherein said electronic control incorporates sensors that measure the position of the edges of said flat metal substrate utilizing infrared light.

5. A process according to claim 1 wherein said preheating of said flat metal substrate is performed by an induction furnace, and the heating power of said induction furnace is controlled by maintaining a relationship to the mass throughput of said flat metal substrate, and said heating power of said induction furnace is additionally controlled by feedback of said laminating temperature, and said laminating temperature is measured on said film-metal laminate by an infrared temperature sensor.

6. A process according to claim 1 wherein said reheating of said film-metal laminate to a post treatment temperature additionally maintains an even surface temperature of said film-metal laminate within 20° F. across the width of said film-metal laminate.

7. A process according to claim 1 wherein any said pretreated major surface of said flat metal substrate is untouched after said pretreating until any said laminating film is pressed against any said pretreated major surface of said flat metal substrate.

8. A process according to claim 1 wherein said flat metal substrate is passivated with iron phosphate, zinc phosphate, or chromium oxide prior to said pretreating of any said major surface of said flat metal substrate, wherein said film-metal laminate is capable of passing a salt spray test per ASTM B 117 with at least 500 hours of testing.

9. A process according to claim 1 wherein said winding temperature is above ambient temperature for the purpose of controlling the crystallinity of said film-metal laminate or for the purpose of improving adhesion in said film-metal laminate, wherein said winding temperature is chosen according to a predetermined criterion.

10. A process according to claim 1 wherein said reheating of said film-metal laminate to said post treatment temperature is performed by an induction furnace, and said induction furnace maintains said film-metal laminate temperature within 20° F. across the width of said film-metal laminate.

11. A process according to claim 1 wherein any temperature controlling roll that is utilized for the purpose of heating or cooling said flat metal substrate or said film-metal laminate maintains a uniform temperature within 20° F. on the surface of said temperature controlling roll.

12. A process according to claim 1 wherein at least one contact cooling roll is used to cool said film-metal laminate to said winding temperature, and said contact cooling roll has a surface finish designed to provide a pre-selected surface gloss to said film-metal laminate surface.

13. A process according to claim 1 wherein a surface flame treatment is utilized to raise the surface energy of any said major surface.

14. A process according to claim 13 wherein said surface flame treatment is also utilized to control said laminating temperature of said flat metal substrate.

15. A process according to claim 1 wherein any of said laminating film is a multi-layered structure with at least two layers.

16. A process according to claim 15 wherein said at least two layers comprises a tie layer and a bulk layer, wherein said tie layer comprises a polyethylene with a maleic anhydride functional group and, an acrylate functional group, said tie layer is next to said flat metal substrate, and said bulk layer comprises a polyester.