Method of absorbing oxygen
View Patent ↗An oxygen-absorbing composition including iron and a soluble tartrate. A method of absorbing oxygen from a closed environment including the steps of providing an oxygen-absorbing composition containing iron and a tartrate, injecting water into the composition, and placing the composition into the closed environment. An oxygen-absorbing packet containing iron and a tartrate. All of the foregoing-mentioned compositions preferably include an electrolyte. The tartrates may be selected from the group which may include solium acid tartrate, potassium acid tartrate, potassium sodium tartrate tetrahydrate and sodium tartrate dihydrate, but are not limited thereto.
1. A method of absorbing oxygen from a closed environment comprising the steps of providing an oxygen-absorbing composition consisting essentially of iron and a tartrate, and injecting water into said composition.
2. A method of absorbing oxygen as set forth in claim 1 wherein said iron is present by weight in an amount of between 55% and 98%, and wherein said tartrate is present by weight in an amount of between about 3% and 50%.
3. A method of absorbing oxygen as set forth in claim 1 wherein said iron is present by weight in an amount of between about 70% and 95% , and wherein said tartrate is present by weight in an amount of between about 5% and 35%.
4. A method of absorbing oxygen as set forth in claim 1 wherein said iron is present by weight in an amount of between about 80% and 90%, and where in said tartrate is present by weight in an amount of between about 10% and 20%.
5. A method of absorbing oxygen as set forth in claim 1 where in said tartrate is selected from the group consisting of potassium acid tartrate, sodium acid tartrate, potassium sodium tartrate tetrahydrate, and sodium tartrate dihydrate.
6. A method of absorbing oxygen as set forth in claim 1 wherein said tartrate is selected from the group consisting of dipotassium tartrate; ammonium tartrate, dibasic; calcium tartrate dihydrate; diethyl tartrate; and diisopropyl tartrate.
7. A method of absorbing oxygen as set forth in claim 1 wherein said composition includes a water-absorbing agent.
8. A method of absorbing oxygen as set forth in claim 7 wherein said iron is present by weight in an amount of between 55% and 98%, and wherein said tartrate is present by weight in an amount of between about 3% and 50% and wherein said water-absorbing agent is present by weight in an amount of between about 1% and 50%.
9. A method of absorbing oxygen as set forth in claim 7 wherein said iron is present by weight in an amount of between about 70% and 95%, and wherein said tartrate is present by weight in an amount of between about 5% and 35% and wherein said water-absorbing agent is present by weight in an amount of between 3% and 30%.
10. A method of absorbing oxygen as set forth in claim 7 wherein said iron is present by weight in an amount of between about 80% and 90%, and wherein said tartrate is present by weight in an amount of between about 10% and 20% and wherein said water-absorbing agent is present by weight in an amount of between 5% and 15%.
11. A method of absorbing oxygen as set forth in claim 7 where in said tartrate is selected from the group consisting of potassium acid tartrate, sodium acid tartrate, potassium sodium tartrate tetrahydrate, and sodium tartrate dihydrate.
12. A method of absorbing oxygen as set forth in claim 7 wherein said tartrate is selected from the group consisting of dipotassium tartrate; ammonium tartrate, dibasic; calcium tartrate dihydrate; diethyl tartrate; and diisopropyl tartrate.
13. A method of absorbing oxygen from a closed environment comprising the steps of providing an oxygen-absorbing composition comprising iron and a tartrate, and injecting water into said composition wherein said tartrate is selected from the group consisting of potassium acid tartrate, sodium acid tartrate, potassium sodium tartrate tetrahydrate, sodium tartrate dihydrate, dipotassium tartrate; ammonium tartrate, dibasic; calcium tartrate dihydrate; diethyl tartrate; and diisopropyl tartrate.
14. A method of absorbing oxygen as set forth in claim 13 wherein said oxygen-absorbing composition includes a water-absorbing agent.
15. A method of absorbing oxygen from a closed environment compising the steps of providing an oxygen-absorbing composition consisting essentially of iron, a tartrate selected from the group consisting of potassium acid tartrate, sodium acid tartrate, potassium sodium tartrate tetrahydrate, sodium tartrate dihydrate, dipotassium tartrate; ammonium tartrate, dibasic; calcium tartrate dihydrate; diethyl tartrate; and diisopropyl tartrate; and an electrolyte, and injecting water into said composition.
16. A method of absorbing oxygen as set forth in claim 15 wherein said composition includes a water-absorbing agent.
17. A method of absorbing oxygen from a closed environment comprising the steps of providing an oxygen-absorbing composition comprising iron, a, tartrate selected from the group consisting of potassium acid tartrate, sodium acid tartrate, potassium sodium tartrate tetrahydrate, sodium tartrate dihydrate, dipotassium tartrate; ammonium tartrate, dibasic; calcium tartrate dihydrate; diethyl tartrate; and diisopropyl tartrate; and an electrolyte, and injecting water into said composition.
18. A method of absorbing oxygen as set forth in claim 17 wherein said oxygen-absorbing composition includes a water-absorbing agent.