Anode-to-cathode capacity ratios for SVO/CF
View Patent ↗Improvements in the performance of lithium electrochemical cells comprising a first cathode active material of a relatively high energy density but of a relatively low rate capability, for example CF x , contacted to one side of a current collector and with a second cathode active material having a relatively low energy density but of a relatively high rate capability, for example SVO, contacted to the opposite current collector side are described. An exemplary cathode has the configuration: SVO/first current collector/CF x /second current collector/SVO, and wherein the anodic coulombic capacity does not exceed the total coulombic capacities of the SVO and CF x by greater than 25%. Manganese oxide (MnO 2 ) is another typically used cathode active material in lieu of SVO, and the present invention is applicable to lithium cells of that system as well.
1. An electrochemical cell, which comprises:
a) an anode of lithium having an anodic coulombic capacity;
b) a cathode comprising the configuration: silver vanadium oxide (SVO)/first current collector/fluorinated carbon (CF x ), wherein in a freshly built cell, a ratio of the anodic coulombic capacity to the total coulombic capacities of SVO and CF x is in a range of: [0.80(M CFx ×Q CFx )+0.40(M SVO ×Q SVO )]<Q anode <[(M CFx ×Q CFx )+(M SVO ×Q SVO )]×1.25, wherein M CFx =the mass of CF x in grams, M SVO =the mass of SVO in grams, Q CFx =the capacity of CF x in mAh, Q SVO =the capacity of SVO in mAh, and Q anode =the capacity of the anode in mAh;
c) a separator disposed between the anode and cathode to prevent direct physical contact between them; and
d) a nonaqueous electrolyte activating the anode and the cathode.
2. The electrochemical cell of claim 1 wherein a ratio of the anodic coulombic capacity to the total coulombic capacities of SVO and CF x is from about 1.15 to about 1.2.
3. The electrochemical cell of claim 1 wherein the SVO faces the anode.
4. The electrochemical cell of claim 1 wherein the cathode has the configuration: SVO/first current collector/CF x /second current collector/SVO.
5. The electrochemical cell of claim 4 wherein a ratio of the anodic coulombic capacity to the total coulombic capacities of SVO and CF x is from about 1.15 to about 1.2.
6. An electrochemical cell, which comprises:
a) an anode of lithium having an anodic coulombic capacity;
b) a cathode having a configuration selected from the group consisting of: SVO/first current collector/CF x /second current collector/SVO and SVO/first current collector/SVO/CF x /SVO/second current collector/SVO, wherein in a freshly built cell, a ratio of the anodic coulombic capacity to the total coulombic capacities of SVO and CF x is in a range of: [0.80(M CFx ×Q CFx )+0.40(M SVO ×Q SVO )]<Q anode <[(M CFx ×Q CFx)+(M SVO ×Q SVO )]×1.25, wherein M CFx =the mass of CF x in grams, M SVO =the mass of SVO in grams, Q CFx =the capacity of CF x in mAh, Q SVO =the capacity of SVO in mAh, and Q anode =the capacity of the anode in mAh;
c) a separator disposed between the anode and cathode to prevent direct physical contact between them; and
d) a nonaqueous electrolyte activating the anode and the cathode.
7. The electrochemical cell of claim 6 wherein a ratio of the anodic coulombic capacity to the total coulombic capacities of the SVO and CF x is from about 1.15 to about 1.2.
8. The electrochemical cell of claim 6 wherein the first and second current collectors are perforated and selected from the group consisting of stainless steel, titanium, tantalum, platinum, gold, aluminum, cobalt nickel alloys, highly alloyed ferritic stainless steel containing molybdenum and chromium, and nickel-, chromium-, and molybdenum-containing alloys.
9. The electrochemical cell of claim 6 wherein the first and second current collectors are titanium having a coating selected from the group consisting of graphite/carbon material, iridium, iridium oxide and platinum provided thereon.
10. An electrochemical cell, which comprises:
a) an anode of lithium;
b) a cathode having a configuration selected from the group consisting of: SVO/first current collector/CF x /second current collector/SVO, SVO/first current collector/SVO/CF x /SVO/second current collector/SVO, SVO/CF x /current collector/CF x /SVO, CF x /first current collector/SVO/second current collector/CF x , and CF x /first current collector/CF x /SVO/CF x /second current collector/CF x , wherein in a freshly built cell, a ratio of the anodic coulombic capacity to the total coulombic capacities of SVO and CF x is in a range of: [0.80(M CFx ×Q CFx )+0.40(M SVO ×Q SVO )]<Q anode <[(M CFx ×Q CFx )+(M SVO ×Q SVO )]×1.25, wherein M CFx =the mass of CF x in grams, M SVO =the mass of SVO in grams, Q CFx =the capacity of CF x in mAh, Q SVO =the capacity of SVO in mAh, and Q anode =the capacity of the anode in mAh;
c) a separator disposed between the anode and cathode to prevent direct physical contact between them; and
d) a nonaqueous electrolyte activating the anode and the cathode.
11. A method for providing an electrochemical cell, comprising the steps of:
a) providing a cathode comprising: silver vanadium oxide (SVO)/first current collector/fluorinated carbon(CF x ), and determining a ratio of the anodic coulombic capacity to the total coulombic capacities of SVO and CF x by the following equation: [0.80(M CFx ×Q CFx )+0.40(M SVO ×Q SVO )]<Q anode <[(M CFx×Q CFx )+(M SVO ×Q SVO )]×1.25, wherein M CFx =the mass of CF x , in grams, M SVO =the mass of SVO in grams, Q CFx =the capacity of CF x in mAh, Q SVO =the capacity of SVO in mAh, and Q anode =the capacity of the anode in mAh;
b) providing an anode comprising lithium having an anodic coulombic capacity;
c) providing the anodic coulombic capacity being equal to or greater than the sum of 40% of the gram amount coulombic capacity of the SVO plus 80% of the gram amount coulombic capacity of the CF x ;
d) providing a separator intermediate the anode and cathode to prevent direct physical contact between them;
e) housing the anode and cathode in a casing; and
f) activating the anode and cathode with a nonaqueous electrolyte provided in the casing.
12. The method of claim 11 including providing a ratio of the anodic coulombic capacity to the total coulombic capacities of the SVO and CF x being from about 1.15 to about 1.2.
13. The method of claim 11 including providing the cathode having the configuration: SVO/first current collector/CF x /second current collector/SVO.
14. The method of claim 13 including providing a ratio of the anodic coulombic capacity to the total coulombic capacities of SVO and CF x is from about 1.15 to about 1.2.