View Patent ↗A threaded joint for a steel pipe comprises a pin and a box with a contact surface having a threaded part and a unthreaded metal contact part, wherein a solid lubricating film containing one or more kinds of lubricating powders selected from graphite, mica, calcium carbonate and kaolin, a copper powder, and a binder is formed on at least one contact surface of the pin and the box. An object of the present invention is to provide a threaded joint for a steel pipe which allows for repeated fastening and loosening of a threaded joint without adversely influencing on a human body and environment, and is excellent in galling resistance, rust preventing property and gas tightness.
1. A threaded joint for a steel pipe comprising a pin and a box with a contact surface having a threaded part and an unthreaded metal contact part,
wherein a solid lubricating film containing at least: a copper powder of which length of the longest part is 1 to 20 μm; a binder, and one or more kinds of lubricating powders selected from the group consisting of graphite, mica, calcium carbonate and kaolin, is formed on at least one contact surface of the pin and the box,
the copper powder is dispersed in the solid lubricating film,
wherein a surface of the copper powder is inactivation-treated, thereby the copper powder has a copper oxide film, a copper sulfide film, or a film of a metal inactivating agent selected from benzotriazole or thiazole on the surface of the copper powder, and
the solid lubricating film is substantially free from molybdenum disulfide and tungsten disulfide.
2. The threaded joint for a steel pipe according to claim 1 , wherein a mass ratio (C/B) of a content (C) of a copper powder to a content (B) of the lubricating powder in the solid lubricating film is 0.5 to 5.0.
3. The threaded joint for a steel pipe according to claim 1 , wherein the solid lubricating film is formed on the contact surface of the box.
4. The threaded joint for a steel pipe according to claim 1 , wherein the solid lubricating film is formed on only the contact surface of one of the pin and the box, and monolayered or di- or more layered films selected from the group consisting of a zinc or zinc alloy film, a metal plating film, a phosphate film, an oxalate film, a borate film and a rust preventing film is formed on the other contacting surface.
5. The threaded joint for a steel pipe according to clam 1 , wherein the solid lubricating film is formed on the contact surface which has been subjected to any undercoating treatment selected from the group consisting of acid washing treatment, blasting treatment, zinc or zinc alloy impact plating treatment, metal plating treatment, soft nitrification treatment, composite metal covering treatment, phosphate treatment and oxalate treatment.
6. The threaded joint for a steel pipe according to claim 1 , wherein the solid lubricating film formed on the contact surface is heat-treated.
7. A method of forming the solid lubricating film on the contact surface of the threaded joint for a steel pipe as defined in claim 1 , which comprises pre-heating the contact surface on which the solid lubricating film is to be formed.