Phosphor composition for a low-pressure discharge lamp with high color temperature
View Patent ↗A phosphor composition for a low-pressure discharge lamp with a high light yield and a high color temperature contains phosphors which emit in the red wavelength region, including yttrium oxide doped with europium or gadolinium-zinc-magnesium pentaborate doped with cerium and manganese, phosphors which emit in the green wavelength region including lanthanum phosphate doped with cerium and terbium and/or cerium-magnesium aluminate doped with terbium and/or cerium-magnesium pentaborate doped with terbium, and optionally a phosphor which emits in the blue wavelength region of the barium-magnesium aluminate doped with europium type. The phosphor composition additionally contains at least one phosphor which emits in the blue or blue-green wavelength region selected from the group consisting of manganese-strontium-barium-magnesium aluminate doped with manganese and europium or barium-magnesium aluminate doped with europium and manganese and strontium aluminate doped with europium and strontium-barium-calcium chloroapatite doped with europium and strontium borophosphate doped with europium.
1. A phosphor composition for a low-pressure discharge lamp with a color rendering index R a greater than 80 and a high color temperature of 8000 K to 20.000 K, the phosphor composition comprising
phosphors which emit in the red wavelength region and which comprise yttrium oxide doped with europium,
phosphors which emit in the green wavelength region and which comprise lanthanum phosphate doped with cerium and terbium, and
at least one phosphor which emits in the blue or blue-green wavelength region, wherein
said europium-doped yttrium oxide forms between 30 and 50% by weight of the phosphor composition,
said cerium- and terbium-doped lanthanum phosphate phosphor forms between 22 and 40% by weight of the phosphor composition, and
said at least one phosphor which emits in the blue or blue-green wavelength region comprises
barium-strontium-magnesium aluminate doped with manganese and europium forming between 10 and 20% by weight of the phosphor composition; or
barium-magnesium alum mate doped with europium and manganese forming between 7 and 35% by weight of the phosphor composition; or
strontium aluminate doped with europium forming between 3 and 15% by weight of the phosphor composition; or
strontium borophosphate doped with europium forming between 3 and 15% by weight of the phosphor composition; and
wherein
the phosphor composition further comprises barium-magnesium aluminate doped with europium forming between 10 and 20% by weight of the phosphor composition as an additional phosphor emitting in the blue wavelength region.
2. The phosphor composition of claim 1 , wherein said europium-doped yttrium oxide forms between 35 and 41% by weight of the phosphor composition.
3. The phosphor composition of claim 1 , wherein said phosphors which emit in the red wavelength region further comprise cerium- and manganese-doped gadolinium-zinc-magnesium pentaborate forming between 5 and 30% by weight of the phosphor composition.
4. The phosphor composition of claim 1 , wherein said cerium- and terbium-doped lanthanum phosphate forms between 30 and 34% by weight of the phosphor composition.
5. The phosphor composition of claim 1 , wherein said manganese- and europium-doped barium-strontium-magnesium aluminate forms between 13 and 17% by weight of the phosphor composition.
6. The phosphor composition of claim 1 , wherein said europium- and manganese-doped barium-magnesium aluminate forms between 10 and 30% by weight of the phosphor composition.
7. The phosphor composition of claim 1 , wherein said europium-doped strontium aluminate forms between 4 and 10% by weight of the phosphor composition.
8. The phosphor composition of claim 1 , wherein said europium-doped strontium borophosphate forms between 4 and 10% by weight of the phosphor composition.
9. A phosphor composition for a low-pressure discharge lamp with a color rendering index R a greater than 80 and a high color temperature of 8000 K to 20.000 K, the phosphor composition comprising
phosphors which emit in the red wavelength region and which comprise yttrium oxide doped with europium,
phosphors which emit in the green wavelength region and which comprise lanthanum phosphate doped with cerium and terbium, and
at least one phosphor which emits in the blue or blue-green wavelength region, wherein
said europium-doped yttrium oxide forms between 30 and 50% by weight of the phosphor composition,
said cerium- and terbium-doped lanthanum phosphate phosphor forms between 22 and 40% by weight of the phosphor composition, and
said at least one phosphor which emits in the blue or blue-green wavelength region comprises europium- and manganese-doped barium-magnesium aluminate phosphor forming between 7 and 20% by weight of the phosphor composition, and wherein said phosphor which emits in the blue or blue-green wavelength region further comprises europium-doped strontium-barium-calcium chloroapatite forming between 20 and 35% by weight of the phosphor composition.
10. The phosphor composition of claim 1 , wherein said phosphors which emit in the green wavelength region further comprise cerium-magnesium aluminate doped with terbium and/or comprise cerium-magnesium pentaborate doped with terbium.
11. A low pressure discharge lamp comprising a discharge vessel having an inner surface wherein at least one layer of phosphor composition is arranged on said inner surface, said phosphor composition having a color rendering index R a greater than 80 and a high color temperature of 8000 K to 20.000 K and said phosphor composition comprising
phosphors which emit in the red wavelength region and which comprise yttrium oxide doped with europium,
phosphors which emit in the green wavelength region and which comprise lanthanum phosphate doped with cerium and terbium, and
at least one phosphor which emits in the blue or blue-green wavelength region, wherein
said europium-doped yttrium oxide forms between 30 and 50% by weight of the phosphor composition,
said cerium- and terbium-doped lanthanum phosphate phosphor forms between 22 and 40% by weight of the phosphor composition, and
said at least one phosphor which emits in the blue or blue-green wavelength region comprises
barium-strontium-magnesium aluminate doped with manganese and europium forming between 10 and 20% by weight of the phosphor composition; or
barium-magnesium aluminate doped with europium and manganese forming between 7 and 35% by weight of the phosphor composition; or
strontium aluminate doped with europium forming between 3 and 15% by weight of the phosphor composition; or
strontium borophosphate doped with europium forming between 3 and 15% by weight of the phosphor composition; and
wherein
the phosphor composition further comprises barium-magnesium aluminate doped with europium forming between 10 and 20% by weight of the phosphor composition as an additional phosphor emitting in the blue wavelength region.
12. A low pressure discharge lamp comprising a discharge vessel having an inner surface wherein at least one layer of phosphor composition is arranged on said inner surface, said phosphor composition having a color rendering index R a greater than 80 and a high color temperature of 8000 K to 20.000 K and said phosphor composition comprising
phosphors which emit in the red wavelength region and which comprise yttrium oxide doped with europium,
phosphors which emit in the green wavelength region and which comprise lanthanum phosphate doped with cerium and terbium, and
at least one phosphor which emits in the blue or blue-green wavelength region, wherein
said europium-doped yttrium oxide forms between 30 and 50% by weight of the phosphor composition,
said cerium- and terbium-doped lanthanum phosphate phosphor forms between 22 and 40% by weight of the phosphor composition, and
said at least one phosphor which emits in the blue or blue-green wavelength region comprises europium- and manganese-doped barium-magnesium aluminate phosphor forming between 7 and 20% by weight of the phosphor composition, and wherein said phosphor which emits in the blue or blue-green wavelength region further comprises europium-doped strontium-barium-calcium chloroapatite forming between 20 and 35% by weight of the phosphor composition.