INFRARED TRANSMISSIVE THERMOPLASTIC COMPOSITION
A thermoplastic composition comprises an aromatic polycarbonate; a polycarbonate-polysiloxane copolymer; and a dye combination comprising a dark color dye, wherein the siloxane domains in the composition have an average domain size of between 15 and 45 nanometers, wherein a molded article having a thickness of 1.0 millimeters comprising the thermoplastic composition has a percent transmission of infrared light of greater than or equal to 65%, when measured at a wavelength of 800 nm, and a dE flop of less than 6.
1 . A thermoplastic composition comprising:
from 0.5 wt. % to 96.99 wt. % of an aromatic polycarbonate;
from 3 wt. % to 99.49 wt. % of a polycarbonate-polysiloxane copolymer; and
from 0.01 wt. % to 5.0 wt. % of a dye combination comprising a dark color dye;
wherein the siloxane domains in the composition have an average domain size of between 15 and 45 nanometers,
wherein a molded article having a thickness of 1.0 millimeters comprising the thermoplastic composition has a percent transmission of infrared light of greater than or equal to 65%, when measured at a wavelength of 800 nm, and
a dE flop of less than 6.
2 . The thermoplastic composition of claim 1 wherein total siloxane content, based on the total composition, is at least 1.5 wt. %.
3 . The thermoplastic composition of claim 1 wherein total siloxane content, based on the total composition, is at least 2.0 wt. %.
4 . The thermoplastic composition of claim 1 wherein total siloxane content, based on the total composition, is at least 2.3 wt. %.
5 . The thermoplastic composition of claim 1 , wherein the dE flop is less than 4.
6 . The thermoplastic composition of claim 1 , wherein a molded article having a thickness of 1.0 millimeters comprising the thermoplastic composition has a percent transmission of infrared light of greater than or equal to 65%, when measured at a wavelength of 1060 nm.
7 . The thermoplastic composition of claim 1 , wherein the dye or dye combination is black.
8 . The thermoplastic composition of claim 1 , wherein a molded article having a thickness of 1.0 millimeters comprising the thermoplastic composition has a percent transmission of infrared light of greater than or equal to 80%, when measured at a wavelength of 800 nm.
9 . The thermoplastic composition of claim 1 , further comprising a flame retardant.
10 . The thermoplastic composition of claim 1 , further comprising a second polycarbonate-polysiloxane copolymer.
11 . An article comprising the thermoplastic composition of claim 1 .
12 . The article of claim 11 , wherein the article is suitable for laser welding.
13 . A thermoplastic composition comprising:
from 50 wt. % to 96.99 wt. % of an aromatic polycarbonate;
from 3 wt. % to 45 wt. % of a polycarbonate-polysiloxane copolymer; and
from 0.01 wt. % to 5.0 wt. % of a dye combination comprising a dark color dye;
wherein the siloxane domains in the composition have an average domain size of between 15 and 45 nanometers and the total siloxane content, based on the total composition, is at least 1.5 wt. %,
wherein a molded article having a thickness of 1.0 millimeters comprising the thermoplastic composition has a percent transmission of infrared light of greater than or equal to 65%, when measured at a wavelength of 800 nm, and
a dE flop of less than 6.
14 . The thermoplastic composition of claim 13 wherein total siloxane content, based on the total composition, is at least 2.0 wt. %.
15 . The thermoplastic composition of claim 13 , wherein the dE flop is less than 4.
16 . The thermoplastic composition of claim 13 , further comprising a second polycarbonate-polysiloxane copolymer.
17 . An article comprising the thermoplastic composition of claim 13 .
18 . The thermoplastic composition of claim 13 , wherein a molded article having a thickness of 1.0 millimeters comprising the thermoplastic composition has a percent transmission of infrared light of greater than or equal to 80%, when measured at a wavelength of 800 nm.
19 . A thermoplastic composition comprising:
from 0.5 wt. % to 96.99 wt. % of an aromatic polycarbonate;
from 3 wt. % to 99.49 wt. % of two polycarbonate-polysiloxane copolymers, wherein at least one polycarbonate-polysiloxane copolymer is transparent; and
from 0.01 wt. % to 5.0 wt. % of a dye combination comprising a dark color dye;
wherein the siloxane domains in the composition have an average domain size of between 15 and 45 nanometers and the total siloxane content, based on the total composition, is at least 1.5 wt. %,
wherein a molded article having a thickness of 1.0 millimeters comprising the thermoplastic composition has a percent transmission of infrared light of greater than or equal to 65%, when measured at a wavelength of 800 nm, and
a dE flop of less than 6.
20 . The thermoplastic composition of claim 19 , wherein the dE flop is less than 4.